Is the high-performance thermoplastic polyetheretherketone indicated as a clasp material for removable dental prostheses?
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Micovic Danka, Mayinger Felicitas, Bauer Sebastian, Roos Malgorzata, Eichberger Marlis, Stawarczyk Bogna
Аннотация
OBJECTIVES: To investigate the retention force of polyetheretherketone (PEEK) removable dental prosthesis clasps in comparison with a cobalt-chrome-molybdenum control group after storage in artificial saliva.
MATERIALS AND METHODS: Clasps were milled (Dentokeep (PEEKmilled1), NT digital implant technology; breCAM BioHPP Blank (PEEKmilled2), bredent), pressed (BioHPP Granulat for 2 press (PEEKpressed), bredent), or cast (remanium GM 800+ (cobalt-chrome-molybdenum), Dentaurum); N = 60, n = 15/subgroup. Retention force was examined 50 times/specimen in a pull-off test using the universal testing machine (Zwick 1445), where pull-off force was applied with a crosshead speed of 5 mm/minute until the maximum force dropped by 10%, at different aging levels: (1) initial, after storage in artificial saliva for (2) 90 and (3) 180 days. Statistical analysis was performed using one-way ANOVA followed by post hoc Scheffé-test and mixed models (p < 0.05).
RESULTS: Cobalt-chrome-molybdenum presented the highest retention force. No differences were observed between polyetheretherketone materials. Cobalt-chrome-molybdenum showed a significant decrease of its values after artificial aging, while polyetheretherketone materials presented similar results over the course of aging. Regarding a repetitive insertion and removal, even though PEEKmilled2 and cobalt-chrome-molybdenum showed an initial increase, ultimately, a decrease in retention force was observed for all tested groups.
CONCLUSIONS: Although the control group showed significantly higher results, the retention force of polyetheretherketone materials indicate a potential clinical application. Neither the manufacturing process nor artificial aging showed an impact on the retention force of polyetheretherketone clasps.
CLINICAL RELEVANCE: Mechanical properties of novel removable dental prosthesis clasp materials devised to meet the growing esthetic demands of patients need to be investigated to ensure a successful long-term clinical application.
MATERIALS AND METHODS: Clasps were milled (Dentokeep (PEEKmilled1), NT digital implant technology; breCAM BioHPP Blank (PEEKmilled2), bredent), pressed (BioHPP Granulat for 2 press (PEEKpressed), bredent), or cast (remanium GM 800+ (cobalt-chrome-molybdenum), Dentaurum); N = 60, n = 15/subgroup. Retention force was examined 50 times/specimen in a pull-off test using the universal testing machine (Zwick 1445), where pull-off force was applied with a crosshead speed of 5 mm/minute until the maximum force dropped by 10%, at different aging levels: (1) initial, after storage in artificial saliva for (2) 90 and (3) 180 days. Statistical analysis was performed using one-way ANOVA followed by post hoc Scheffé-test and mixed models (p < 0.05).
RESULTS: Cobalt-chrome-molybdenum presented the highest retention force. No differences were observed between polyetheretherketone materials. Cobalt-chrome-molybdenum showed a significant decrease of its values after artificial aging, while polyetheretherketone materials presented similar results over the course of aging. Regarding a repetitive insertion and removal, even though PEEKmilled2 and cobalt-chrome-molybdenum showed an initial increase, ultimately, a decrease in retention force was observed for all tested groups.
CONCLUSIONS: Although the control group showed significantly higher results, the retention force of polyetheretherketone materials indicate a potential clinical application. Neither the manufacturing process nor artificial aging showed an impact on the retention force of polyetheretherketone clasps.
CLINICAL RELEVANCE: Mechanical properties of novel removable dental prosthesis clasp materials devised to meet the growing esthetic demands of patients need to be investigated to ensure a successful long-term clinical application.