UNLABELLED: Calcium aluminate cement (CAC) has been highlighted as a promising alternative for endodontic use aiming at periapical tissue repair. However, its effects on dental pulp cells have been poorly explored.

OBJECTIVE

This study assessed the impact of calcium chloride (CaCl2) and bismuth oxide (Bi2O3) or zinc oxide (ZnO) additives on odontoblast cell response to CAC.

METHODOLOGY: MDPC-23 cells were exposed for up to 14 d: 1) CAC with 2.8% CaCl2 and 25% ZnO (CACz); 2) CAC with 2.8% CaCl2 and 25% Bi2O3 (CACb); 3) CAC with 10% CaCl2 and 25% Bi2O3 (CACb+); or 4) mineral trioxide aggregate (MTA), placed on inserts. Non-exposed cultures served as control. Cell morphology, cell viability, gene expression of alkaline phosphatase (ALP), bone sialoprotein (BSP), and dentin matrix protein 1 (DMP-1), ALP activity, and extracellular matrix mineralization were evaluated. Data were compared using ANOVA (α=5%).

RESULTS

Lower cell density was detected only for MTA and CACb+ compared with Control, with areas showing reduced cell spreading. Cell viability was similar among groups at days one and three (p>0.05). CACb+ and MTA showed the lowest cell viability values at day seven (p>0.05). CACb and CACb+ promoted higher ALP and BSP expression compared with CACz (p<0.05); despite that, all cements supported ALP activity. Matrix mineralization were enhanced in CACb+ and MTA.

CONCLUSION

In conclusion, CAC with Bi2O3, but not with ZnO, supported the expression of odontoblastic phenotype, but only the composition with 10% CaCl2 promoted mineralized matrix formation, rendering it suitable for dentin-pulp complex repair.