Syngas production and gas-N evolution over heterogeneously doped La-Fe-O perovskite-type oxygen carriers in chemical looping gasification of microalgae.

Chemical looping gasification (CLG) is a promising technology for syngas production with low pollutant emission. In this study, doped La-Fe-O perovskites including LaFeO3 (LF), LaFe0.5Ni0.5O3 (LN5F5) and La0.3Ba0.7FeO3 (L3B7F) were developed for microalgae CLG. The as-prepared perovskites exhibited an outstanding performance in syngas production with accumulative syngas yield > 33 mol/kg. For gas-N evolution, perovskites were beneficial to the formation of NH3 and HCN, while the iron ore may convert precursors to NO. Below 400 °C, NOx can be stored on the perovskite surface in the form of nitrite/nitrate species. When the temperature was above 700 °C, NOx can be selectively reduced by reducing components in tar or syngas under the catalysis of L3B7F, resulting in the final reduction of NOx emission. Thus, CLG over L3B7F may be a promising way for efficient utilization of microalgae to overcome the intractable nitrogen-related obstacles in the commercial application of biomass gasification technologies.