International endodontic journal · 2011
Dynamic sealing ability of MTA root canal sealer.
Оценочное исследованиеСтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Camilleri J, Gandolfi M G, Siboni F, Prati C
Аннотация
AIMS: To evaluate (i) the sealing ability of two sealers, mineral trioxide aggregate sealer (MTAS) and Pulp Canal Sealer (PCS), used with gutta-percha utilizing the fluid filtration method, (ii) leaching and surface characteristics in Hank's balanced salt solution (HBSS) over a period of time.
METHODOLOGY: Surface characteristics in HBSS were evaluated under the scanning electron microscope after 1 and 28 days, and the leaching of both sealers were assessed by inductively coupled plasma atomic absorption spectrometry (ICP-AAS). In addition, 24 single rooted extracted teeth were root filled using warm vertical compaction with either MTAS or PCS used as sealers with gutta-percha. Four teeth were used as positive and negative controls. Sealing ability was evaluated after 1 or 28 days using the fluid filtration method.
RESULTS: Mineral trioxide aggregate sealer exhibited crystalline deposits rich in calcium and phosphorus on its surface when in contact with a physiological solution. These crystalline deposits were absent in PCS and on MTAS stored at 100% humidity. The sealing ability of MTAS was similar to that of PCS.
CONCLUSIONS: The novel sealer based on mineral trioxide aggregate had comparable sealing ability to a proprietary brand sealer cement. In contact with a simulated body fluid, the MTA sealer released calcium ions in solution that encouraged the deposition of calcium phosphate crystals.
METHODOLOGY: Surface characteristics in HBSS were evaluated under the scanning electron microscope after 1 and 28 days, and the leaching of both sealers were assessed by inductively coupled plasma atomic absorption spectrometry (ICP-AAS). In addition, 24 single rooted extracted teeth were root filled using warm vertical compaction with either MTAS or PCS used as sealers with gutta-percha. Four teeth were used as positive and negative controls. Sealing ability was evaluated after 1 or 28 days using the fluid filtration method.
RESULTS: Mineral trioxide aggregate sealer exhibited crystalline deposits rich in calcium and phosphorus on its surface when in contact with a physiological solution. These crystalline deposits were absent in PCS and on MTAS stored at 100% humidity. The sealing ability of MTAS was similar to that of PCS.
CONCLUSIONS: The novel sealer based on mineral trioxide aggregate had comparable sealing ability to a proprietary brand sealer cement. In contact with a simulated body fluid, the MTA sealer released calcium ions in solution that encouraged the deposition of calcium phosphate crystals.
Предметные рубрики MeSH
Aluminum CompoundsAnalysis of VarianceCalcium CompoundsCalcium PhosphatesDental LeakageDrug CombinationsGutta-PerchaHumansIsotonic SolutionsMaterials TestingMicroscopy, Electron, ScanningOxidesRoot Canal Filling MaterialsRoot Canal ObturationSilicatesSpectrometry, X-Ray EmissionSpectrophotometry, AtomicSurface PropertiesZinc Oxide-Eugenol Cement