Journal of dentistry · 2006
MAS-NMR spectroscopy studies in the setting reaction of glass ionomer cements.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Stamboulis A, Matsuya S, Hill R G, Law R V, Udoh K, Nakagawa M, Matsuya Y
Аннотация
OBJECTIVES: The main objective is the characterisation of the setting reaction in glass ionomer cements based on experimental ionomer glasses with different fluorine content and a commercial glass ionomer cement liquid by using 13C CP/MAS-NMR, 29Si, 27Al and 31P MAS-NMR spectroscopy in order to receive information specifically about the cross-linking process.
METHODS: Different fluorine containing glass compositions based on 4.5SiO2-3Al2O3-1.5P2O5-(5-z)CaO-zCaF(2) where z=0-3, were mixed with a commercially available polymer liquid to form glass ionomer cements. The cements were subjected to 27Al, 13C CP/MAS, 29Si, and 31P MAS-NMR analysis.
RESULTS: The 27Al spectra showed clearly the formation of six-fold coordinate Al(VI), that may crosslink the carboxyl groups in the poly-acid molecules. A shift towards to more positive values of the carboxyl peak in the 13C CP/MAS-NMR spectra showed clearly the proton dissociation of the carboxyl groups. A shift towards more negative values was observed in the 29Si MAS-NMR spectra, suggesting formation of hydrated silica gel and consequently formation of additional Si-O-Si bonds. 31P MAS-NMR spectra also reflected changes in the coordination state around a PO4(3-) tetrahedron. Increasing the fluorine content of the glasses resulted generally in increased reactivity during setting, due to promoting cross-linking and repolymerisation of the silicate phase, followed by clear changes in the MAS-NMR spectra.
CONCLUSIONS: The cross-linking process during the setting reaction of glass ionomer cements can be followed by MAS-NMR spectroscopy observing the conversion of Al(IV) to Al(VI). The acid base setting reaction is completed in 1 day and no further significant changes in the MAS-NMR spectra can be observed. Further study is required in order to understand the role of phosphorus.
METHODS: Different fluorine containing glass compositions based on 4.5SiO2-3Al2O3-1.5P2O5-(5-z)CaO-zCaF(2) where z=0-3, were mixed with a commercially available polymer liquid to form glass ionomer cements. The cements were subjected to 27Al, 13C CP/MAS, 29Si, and 31P MAS-NMR analysis.
RESULTS: The 27Al spectra showed clearly the formation of six-fold coordinate Al(VI), that may crosslink the carboxyl groups in the poly-acid molecules. A shift towards to more positive values of the carboxyl peak in the 13C CP/MAS-NMR spectra showed clearly the proton dissociation of the carboxyl groups. A shift towards more negative values was observed in the 29Si MAS-NMR spectra, suggesting formation of hydrated silica gel and consequently formation of additional Si-O-Si bonds. 31P MAS-NMR spectra also reflected changes in the coordination state around a PO4(3-) tetrahedron. Increasing the fluorine content of the glasses resulted generally in increased reactivity during setting, due to promoting cross-linking and repolymerisation of the silicate phase, followed by clear changes in the MAS-NMR spectra.
CONCLUSIONS: The cross-linking process during the setting reaction of glass ionomer cements can be followed by MAS-NMR spectroscopy observing the conversion of Al(IV) to Al(VI). The acid base setting reaction is completed in 1 day and no further significant changes in the MAS-NMR spectra can be observed. Further study is required in order to understand the role of phosphorus.