Preparation of new hydrogels by visible light cross-linking of dextran methacrylate and poly(ethylene glycol)-maleic acid copolymer.

In this work, a series of new biodegradable and biocompatible hydrogels were synthesized by photopolymerization of dextran-methacrylate (DXM) with poly(ethylene glycol)-maleic acid copolymer (poly(PEG-co-MA, PEGMA)) using (-)-riboflavin as a visible light photoinitiator and L-arginine as a co-photoinitiator. DXM was prepared by acylation of dextran (DX) with methacryloyl chloride (MAC), and PEGMA was synthesized by polycondensation of poly(ethylene glycol) (PEG) and maleic acid (MA). The DXM and PEGMA were characterized by FT-IR and 1HNMR spectroscopy. Different types of hydrogels from various ratios of DXM and PEGMA were prepared and characterized by SEM. The results showed that the prepared hydrogel by photo-cross-linking of DXM (DPHG0) was transparent and flexible, and its physical shape was excellent, but it was sticky. The stickiness was reduced by increasing the PEGMA contents, and different types of DXM/PEGMA hydrogels (DPHG1-4) with various properties were prepared. For example, DPHG2 (PEGMA content was 0.25 g) was transparent and flexible, its physical shape was excellent, and it was not sticky. The prepared hydrogels showed excellent cytocompatibility, and their tensile and compressive strength were also evaluated. Additionally, the in vitro degradation and swelling ratios of the prepared hydrogels were studied in buffer solution at different pHs.