Enhanced burst strength of catechol groups-modified Alaska pollock-derived gelatin-based surgical adhesive.

Aortic anastomotic leak is a potentially fatal complication that can occur after treatment of aortic dissection or aneurysm. Several surgical adhesives have been used to prevent this complication, but all have problems with regard to tissue adhesion or biocompatibility. In the present study, we developed a surgical adhesive composed of boric acid-protected catechol groups-modified Alaska pollock-derived gelatin (Cat-ApGltn) and a poly(ethylene glycol)-based crosslinker (4S-PEG). By avoiding oxidation of catechol groups using boric acid, resulting Cat-ApGltn adhesive formed a strong hydrogel by double crosslinking: chemical crosslinking by 4S-PEG, and chemical and physical crosslinking by the catechol groups. The catechol groups modification contributed to increased bulk strength and decreased gelation time/swelling ratios. The Cat-ApGltn adhesive, in which 7.8 mol% of the amino groups of the original ApGltn (Org-ApGltn) were modified with catechol groups, demonstrated 2.3 times higher burst strength compared with the Org-ApGltn adhesive, and 3.9 times higher burst strength compared with a commercial fibrin adhesive. When the Cat-ApGltn adhesive was implanted subcutaneously into rats, it induced only weak inflammation similar to that induced by the Org-ApGltn adhesive, and was completely degraded within 2 months. Therefore, the Cat-ApGltn adhesive has great potential for use in the field of cardiovascular surgery.