Nanosphere size control by varying the ratio of poly(ester amide) block copolymer blends.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Lima Mariana R N, Devore David I, Kohn Joachim
Аннотация
HYPOTHESIS: Blending amphiphilic triblock (A-B-A) and diblock (A-B) copolymers comprised of the same hydrophobic tyrosine-derived oligomeric B-block and hydrophilic poly(ethylene glycol) methyl ether (mPEG) A-block can provide highly tunable self-assembled nanosphere particle sizes suitable for biomedical applications.
EXPERIMENT: Triblock and diblock copolymers were synthesized via carbodiimide chemistry and were characterized by nuclear magnetic resonance (NMR) and gel permeation chromatography (GPC). The amount of free PEG present in the purified copolymers was determined using a standard addition calibration curve and GPC peak deconvolution methods. Nanospheres were prepared by co-precipitation of each copolymer and of copolymer blends over a range of mole ratios. Nanospheres were characterized by dynamic light scattering (DLS), transmission electron microscopy (TEM) and % polymer recovery post-preparation.
FINDING: Precise synthesis control produced triblock and diblock copolymers with narrow molecular weight distributions and minimal residual reactants. Self-assembled nanosphere particle sizes were 33 nm for the triblock and 129 nm for the diblock, and the size of their blends increased continuously as a function of mole ratio within that biomedically relevant range. Addition of unreacted PEG had minimal impact on either triblock or diblock nanosphere particle sizes whereas addition of unreacted oligomeric B-block increased nanosphere sizes.
EXPERIMENT: Triblock and diblock copolymers were synthesized via carbodiimide chemistry and were characterized by nuclear magnetic resonance (NMR) and gel permeation chromatography (GPC). The amount of free PEG present in the purified copolymers was determined using a standard addition calibration curve and GPC peak deconvolution methods. Nanospheres were prepared by co-precipitation of each copolymer and of copolymer blends over a range of mole ratios. Nanospheres were characterized by dynamic light scattering (DLS), transmission electron microscopy (TEM) and % polymer recovery post-preparation.
FINDING: Precise synthesis control produced triblock and diblock copolymers with narrow molecular weight distributions and minimal residual reactants. Self-assembled nanosphere particle sizes were 33 nm for the triblock and 129 nm for the diblock, and the size of their blends increased continuously as a function of mole ratio within that biomedically relevant range. Addition of unreacted PEG had minimal impact on either triblock or diblock nanosphere particle sizes whereas addition of unreacted oligomeric B-block increased nanosphere sizes.