Journal of prosthodontics : official journal of the American College of Prosthodontists · 2015
In Vitro Wear Resistance of Nano-Hybrid Composite Denture Teeth.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Munshi Nabeel, Rosenblum Marc, Jiang Shuying, Flinton Robert
Аннотация
PURPOSE: To evaluate the wear resistance of nano-hybrid composite denture teeth as compared to two commonly used denture teeth: interpenetrating polymer network (IPN) and double crosslinking polymethylmethacrylate (PMMA) denture teeth.
MATERIAL AND METHODS: 18 styli and 18 disk specimens were prepared from the three denture tooth materials: nano-hybrid composite, IPN, and double crosslinking PMMA. The specimens were mounted in a two-body wear testing machine to simulate chewing in the complete denture. The amount of wear from the styli specimens were measured before and after using a digital micrometer, and the depth of the wear track from the disk specimens was measured using a noncontact 3D optical profilometer. The total wear from each denture tooth group was compared using one-way ANOVA with a 0.05 significance level. A Tukey post hoc test was used to determine differences between the three groups.
RESULTS: The mean total wear in the nano-hybrid composite teeth group was 1.16 mm, SD = 0.5 mm, statistically significantly higher (p ≤ 0.0001) than the IPN (mean = 0.13 mm, SD = 0.05) and double crosslinking PMMA tooth groups (mean = 0.31 mm, SD = 0.19). There was no statistically significant difference between IPN denture teeth and double crosslinking PMMA denture teeth in the amount of wear.
CONCLUSIONS: Nano-hybrid composite denture teeth exhibited statistically significantly more wear than the IPN and double crosslinking PMMA denture teeth.
MATERIAL AND METHODS: 18 styli and 18 disk specimens were prepared from the three denture tooth materials: nano-hybrid composite, IPN, and double crosslinking PMMA. The specimens were mounted in a two-body wear testing machine to simulate chewing in the complete denture. The amount of wear from the styli specimens were measured before and after using a digital micrometer, and the depth of the wear track from the disk specimens was measured using a noncontact 3D optical profilometer. The total wear from each denture tooth group was compared using one-way ANOVA with a 0.05 significance level. A Tukey post hoc test was used to determine differences between the three groups.
RESULTS: The mean total wear in the nano-hybrid composite teeth group was 1.16 mm, SD = 0.5 mm, statistically significantly higher (p ≤ 0.0001) than the IPN (mean = 0.13 mm, SD = 0.05) and double crosslinking PMMA tooth groups (mean = 0.31 mm, SD = 0.19). There was no statistically significant difference between IPN denture teeth and double crosslinking PMMA denture teeth in the amount of wear.
CONCLUSIONS: Nano-hybrid composite denture teeth exhibited statistically significantly more wear than the IPN and double crosslinking PMMA denture teeth.