Study on Microstructure and Property Regulation of 18Ni350 Maraging Steel Fabricated by Selective Laser Melting and Its Corrosion Resistance to Molten Aluminum.

The influence of different heat treatment processes on the microstructure and mechanical properties of 18Ni350 maraging steel manufactured by selective laser melting and the corrosion resistance of TiB2 ceramic coatings Electro-Spark-Deposited on its surface when immersed in high-temperature molten aluminum have been investigated in the present study. The microstructures and mechanical properties of the differently heat-treated samples were analyzed using various precision instruments. The results reveal that the as-built sample exhibits a microstructure composed of cellular and columnar dendritic grains. After solution treatment, the microstructure fully transforms into lath-like martensite. After direct aging treatment, the cellular structures diminish, while precipitates at grain boundaries proliferate with increasing aging temperature. SAT- treatment achieves full microstructural homogenization, featuring fine-lath martensite and a small amount of randomly distributed austenite particles. DA- and SAT- significantly improve the strength, hardness and modulus of samples and were found to reduce the toughness and plasticity. After solution treatment at 800 °C for 1 h followed by aging treatment at 520 °C for 6 h (SAT 800-520), the specimen achieved an UTS of 2476 MPa while maintaining an EL of 4.6%. The TiB2 coating and the Cr interlayer deposited via ESD form a continuous interfacial bond with the substrate, demonstrating favorable adhesion. After 4 h of static immersion in high-temperature molten aluminum, the coating remains intact without complete delamination, delivering effective protection to the substrate.