Mechanical Behavior of Conventional and Subtractively Manufactured Dental Resin Composites After Water Degradation.

The ongoing development of subtractive options for indirect restorations places clinicians in a position that requires adaptation, understanding and choosing of the most suitable option for the long-term survival of the restoration. Mechanical parameters represent important indicators of long-term success. Consequently, this research aimed to assess the impact of water sorption on the mechanical properties of two direct resin composites, Gradia Direct Anterior A2 and Filtek Z550 A2 and three CAD/CAM subtractively manufactured dental resin composites, Vita Enamic, Brilliant and Cerasmart. A total of one hundred specimens (50 control, 50 underwent this protocol: dehydration, immersion in distilled water for 30 days and then re-desiccation), standardized to the dimensions of 14 mm × 4 mm × 1.2 mm were subjected to three-point bending test (based on ISO 4049:2019 and ISO 6872:2015), in order to find out the flexural strength and the elastic modulus of the material at the breaking point. Then, the fractured sample surfaces were fractographical analyzed. Using the two-parameter Weibull approach, the Weibull modulus (m) and the characteristic strength (σ0) were evaluated. In this investigation, the elastic modulus varied from 5.8 (Gradia Control) to 20.31 (Vita Degraded) GPa, with the upper limit close to the values of natural dentin (17.7-29.8 GPa). The values of flexural strength ranged from 174.47 (Brilliant Control) to 79.2 (Gradia Control), subtractively processed materials demonstrating higher flexural strength and elastic modulus values than the direct resin composites, which is related to their high inorganic filler content. All material groups, except for Gradia Control, had a flexural strength more than the 80 MPa minimum value needed to sustain masticatory force. The dehydration and hydration cycles did not have a statistically significant influence on the mechanical properties of the material. The fractographic analysis revealed fracture patterns and features associated with the microstructure, with the PICN category material being particularly notable. Weibull analysis revealed that the direct resin composite materials exhibited higher reliability, lower data scatter and CAD-CAM materials showed greater characteristic strength, with a notably high performance of the nano-hybrid direct resin composite.