Rapid Formation and Interfacial Adhesion Enhancement in Zirconium Conversion Coatings on 55AlZnMg-Coated Steel Under a Short H2ZrF6 Pretreatment.

To address the uneven deposition of zirconium conversion coatings on multiphase 55AlZnMg under short pretreatment cycles, this study investigated the time-dependent formation behavior of ZrCC in a selected H2ZrF6 bath. By precisely controlling the immersion time (20-90 s) and utilizing SEM-EDS and AFM characterization techniques, this study systematically revealed the growth kinetics and film-forming mechanisms of ZrCC on complex alloy surfaces. The results indicate that the Zn-rich phase on the surface of the 55AlZnMg coating, due to its relatively positive potential, preferentially induces the deposition of the film-forming material. Subsequently, dealloying occurs in the Al-rich phase and the Mg/Zn enriched regions, forming Zn-enriched regions that promote the continuous deposition of the film-forming material, ultimately achieving complete surface coverage; the film morphology evolves from an initial needle-like structure to a network structure, eventually forming a nanosheet structure. The film-forming process of ZrCC on the 55AlZnMg substrate surface is primarily driven by selective growth, with electrochemical properties of the alloy phases, significantly enhancing adhesion between the aluminum-zinc-magnesium coating and the overcoat and providing practical guidance for improving surface uniformity and interfacial adhesion of Al-Zn-Mg-coated steel.