The effect of autoclave cycles on the mechanical properties and surface roughness of NiTi archwires: ex-vivo study.

OBJECTIVES

To evaluate the effect of the universal and rapid autoclave cycles on the mechanical properties and surface roughness of nickel-titanium archwires following clinical use.

MATERIAL AND

METHODS

Thirty-six NiTi archwires (0.016 × 0.022 inch) were equally divided into a control group (Group A) and 2 experimental groups (Group B & C). Wires in group A were tested in the "as-received" form. Wires in the two other groups were installed in patients mouth for 4 weeks, and then autoclaved using the rapid-cycle (Group B) or the universal-cycle (Group C). All wires were subjected to 3-point bending test to calculate the elastic limit, modulus of elasticity, spring-back, yield strength, resilience and toughness. Atomic force microscopy (AFM) was used for surface roughness qualitative and quantitative analysis.

RESULTS

Group B showed significantly higher values of elastic limit, modulus of elasticity, resilience, yield strength and toughness than the other two groups. No significant differences were detected between groups A and C (P > 0.05). Group B showed significantly lower average surface roughness than the other two groups, but no significant differences were detected between groups A and C (P > 0.05).

CONCLUSIONS

The mechanical properties and surface roughness of clinically used NiTi wires were less affected by the universal-cycle than the rapid-cycle autoclaving. However, the difference between the effect of both autoclave cycles was diminutive.

CLINICAL RELEVANCE: The mechanical properties and surface roughness of the tested NiTi wires were not notably altered by clinical use and autoclaving.