Geometry-Driven Structural Efficiency and Normative Performance of Miriti-Based Sandwich Composite Roofing Tiles.

This work experimentally evaluates the geometry-driven structural efficiency and normative performance of sandwich-type composite roofing tiles composed of a miriti wood core and fiberglass-reinforced polymer faces. Trapezoidal-profile tiles were manufactured by hand lay-up and assessed according to ABNT NBR 16753, including visual inspection, fiber content, water absorption, apparent flexural behavior, deformation resistance, and impact resistance. The miriti core exhibited an extremely low mean density of 0.091 ± 0.008 g/cm3 (CV ≈ 8.8%), enabling lightweight sandwich configurations with an average overall thickness of approximately 8 mm. Fiberglass contents ranged from 27.5% to 32.1% by mass. Sealed sandwich specimens showed median water uptake values of approximately 2.5% after 2 h and 6.0% after 24 h immersion. Deformation resistance tests indicated admissible deflections of 15.0-15.75 mm (L/40), supported by applied masses between 39.6 and 104.3 kg (≈388-1023 N) without rupture or permanent damage. Apparent flexural stresses ranged from 6.7 to 9.3 MPa, with apparent moduli between 0.7 and 1.9 GPa. All tiles achieved 100% approval in deformation, impact (2-8 J), and visual criteria. The results demonstrate that geometric effects dominate structural performance, validating miriti wood as an efficient and sustainable core for normatively compliant composite roofing systems.