Magnetic-Field-Induced Improvement of Photothermal Sterilization Performance by Fe3O4@SiO2@Au/PDA Nanochains.

Due to the abuse of antibiotics, the sensitivity of patients to antibiotics is gradually reduced. This work develops a Fe3O4@SiO2@Au/PDA nanochain which shows an interesting magnetic-field-induced improvement of its photothermal antibacterial property. First, SiO2 was wrapped on Fe3O4 nanospheres assembled in a chain to form a Fe3O4@SiO2 nanocomposite with a chain-like nanostructure. Then, the magnetic Fe3O4@SiO2@Au/PDA nanochains were prepared using in situ redox-oxidization polymerization. Under the irradiation of an 808 nm NIR laser, the temperature rise of the Fe3O4@SiO2@Au/PDA nanochain dispersion was obvious, indicating that they possessed a good photothermal effect. Originating from the Fe3O4, the Fe3O4@SiO2@Au/PDA nanochain showed a typical soft magnetic behavior. Both the NIR and magnetic field affected the antimicrobial performance of the Fe3O4@SiO2@Au/PDA nanochains. Escherichia coli and Staphylococcus aureus were used as models to verify the antibacterial properties. The experimental results showed that the Fe3O4@SiO2@Au/PDA nanochains exhibited good antibacterial properties under photothermal conditions. After applying a magnetic field, the bactericidal effect was further significantly enhanced. The above results show that the material has a broad application prospect in inhibiting the growth of bacteria.