Biomaterial investigations in dentistry · 2025
One year monitoring of calcium release from an experimental composite containing calcium phosphate particles.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Vilela Handially, Nakamura Mariana, Braga Roberto
Аннотация
INTRODUCTION: Ca2+ release from specimens made of a composite containing dicalcium phosphate dihydrate particles (CaHPO4.2H2O, dicalcium phosphate dihydrate [DCPD]) was followed during 1 year.
METHODS: Specimens were individually immersed in deionized water (n = 3). Every 2 weeks, immersion medium was collected and specimens were transferred to new vials with fresh medium. Ca2+ release was quantified using induced coupled plasma-optical emission spectrometry (ICP-OES). Data were analyzed by ANOVA/Tukey test (alpha: 5%).
RESULTS: Ca2+ release was observed during the entire 12-month period. Cumulative release was 1635.1 ± 145.3 μg/cm2 (179.7 ± 16.0 ppm), corresponding to 23.8 ± 2.0% of the total Ca mass in the specimen.
CONCLUSION: The tested composite was capable of sustained Ca2+ release in water for 1 year. In spite of the limitations of this screening test, the results suggest that composites containing Calcium phosphate (CaP) particles could offer a long-term Ca2+ supply to the adjacent dental tissues.
METHODS: Specimens were individually immersed in deionized water (n = 3). Every 2 weeks, immersion medium was collected and specimens were transferred to new vials with fresh medium. Ca2+ release was quantified using induced coupled plasma-optical emission spectrometry (ICP-OES). Data were analyzed by ANOVA/Tukey test (alpha: 5%).
RESULTS: Ca2+ release was observed during the entire 12-month period. Cumulative release was 1635.1 ± 145.3 μg/cm2 (179.7 ± 16.0 ppm), corresponding to 23.8 ± 2.0% of the total Ca mass in the specimen.
CONCLUSION: The tested composite was capable of sustained Ca2+ release in water for 1 year. In spite of the limitations of this screening test, the results suggest that composites containing Calcium phosphate (CaP) particles could offer a long-term Ca2+ supply to the adjacent dental tissues.