Triple Corrosion Protection: Dual-Layer Coating with Simultaneous Superhydrophobicity, Intelligent Self-Healing, and Shape Memory.

In this paper, a self-healing superhydrophobic smart two-layer coating, ZOA/SMP-S, was developed. ZIF-8 was surface hydrophobically modified by octadecylphosphoric acid (OPA) to obtain Z-OPA and then encapsulated with a corrosion inhibitor, AMT ( 2-Amino-5-mercapto-1,3,4-thiadiazole), to obtain the superhydrophobic nanocontainers, ZOA. ZOA was embedded into the SMP (shape memory coating) to obtain the smart coating, and Z-OPA was sprayed to obtain the second superhydrophobic coating. SEM showed that the scratch coatings were rapidly reduced by scratches after a simple heat treatment. The prepared composite coatings showed excellent performance in corrosion inhibitor release, immersion, superhydrophobicity, and self-healing experiments. The contact angle of the superhydrophobic coating reached 158.2°, and the sliding angle was 2.8°. The low-frequency impedance value |Z|f=0.01 Hz of ZOA/SMP-S is as high as 1.58 × 1010 Ω·cm2 after 40 days of immersion test, which indicates that the triple protection greatly enhances the corrosion resistance of the coating.