Biomineralization reaction from nanosized calcium silicate: A new method for reducing dentin hypersensitivity.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Jeon Mi-Jeong, Choi Yu-Sung, Park Jeong-Kil, Ahn Jin-Soo, Chiang Yu-Chih, Seo Deog-Gyu
Аннотация
BACKGROUND/PURPOSE: This study assessed the ability of experimental materials consisting of dicalcium silicate (DCS) and tricalcium silicate (TCS) with nanosized particles to form intratubular crystals under phosphate-buffered saline (PBS) and the effect on dentin permeability reduction.
MATERIALS AND METHODS: By isolating the cervical part of the extracted premolars, 195 specimens were obtained. Two experimental materials (DCS/TCS and TCS) were applied to the dentin surface by brushing and stored in PBS (n = 65). Another 65 specimens were not treated. Each group was randomly divided into five subgroups based on the PBS immersion period (1, 15, 30, 60, and 90 days, n = 10). The dentin permeability was measured, and the hydraulic conductance, Lp (%), was calculated. After acid challenge with 1 M acetic acid, Lp (%) was remeasured. Data were analyzed using two-way analysis of variance and Fisher's least significant difference test (α = 0.05). Three specimens of each subgroup were longitudinally sectioned and examined using scanning electron microscopy and a field emission-electron probe micro analyzer.
RESULTS: The Lp (%) of the experimental groups gradually decreased over time (P < 0.05). The hydroxyapatite-like crystals that grew were observed and found to have a Ca/P ratio similar to that of hydroxyapatite. The crystals remained after the acid challenge, and the Lp (%) was not significantly different from that before acid treatment.
CONCLUSION: Intratubular crystals formed from the experimental materials consisted of DCS and TCS and were resistant to acid. These crystals significantly reduced dentin permeability.
MATERIALS AND METHODS: By isolating the cervical part of the extracted premolars, 195 specimens were obtained. Two experimental materials (DCS/TCS and TCS) were applied to the dentin surface by brushing and stored in PBS (n = 65). Another 65 specimens were not treated. Each group was randomly divided into five subgroups based on the PBS immersion period (1, 15, 30, 60, and 90 days, n = 10). The dentin permeability was measured, and the hydraulic conductance, Lp (%), was calculated. After acid challenge with 1 M acetic acid, Lp (%) was remeasured. Data were analyzed using two-way analysis of variance and Fisher's least significant difference test (α = 0.05). Three specimens of each subgroup were longitudinally sectioned and examined using scanning electron microscopy and a field emission-electron probe micro analyzer.
RESULTS: The Lp (%) of the experimental groups gradually decreased over time (P < 0.05). The hydroxyapatite-like crystals that grew were observed and found to have a Ca/P ratio similar to that of hydroxyapatite. The crystals remained after the acid challenge, and the Lp (%) was not significantly different from that before acid treatment.
CONCLUSION: Intratubular crystals formed from the experimental materials consisted of DCS and TCS and were resistant to acid. These crystals significantly reduced dentin permeability.