Effect of heat sterilization and chemical method of sterilization on the polyvinyl siloxane impression material. A comparative study.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Asopa Swati Joshi, Padiyar U Narendra, Verma Sumit, Suri Prerna, Somayaji Nagaveni S, Radhakrishnan Indu Cherangapadath
Аннотация
BACKGROUND: Dental impression is a crucial part of the process of constructing a well-fitting prosthesis. In the clinical scenario, impressions can act as a vehicle for the transfer of bacteria and fungi. Therefore, an attempt was made to evaluate the dimensional accuracy of the newly introduced polyvinyl siloxane (PVS) impression material upon autoclaving and comparing it to the traditional means of chemical disinfection.
MATERIALS AND METHODS: A cross-sectional comparative in vitro study was conducted. Three groups were made for testing different sterilization methods. The sample size for the study was kept as 30 observations in each of the three groups. Test samples were prepared by making an impression of the die using the putty-wash technique. Statistical analysis was done by applying unpaired t-test, paired t-test, one-way analysis of variance (ANOVA) and post hoc Tukey's honestly significant difference (HSD).
RESULTS: Initial mean of samples of group I were compared to A (actual measurement of metal ruled block = 24.960), a dimensional change of 1.6% was found. Similarly, in group II, a change of 1.59% was found and in group III the change was 1.7%. There was mean shrinkage of 24.557 mm in group I, 24.586 mm in group II, and 24.535 mm in group III and these changes were found statistically significant.
CONCLUSION: Dimensional changes in the impression material after disinfection with 2% glutaraldehyde were considered high compared to autoclaving and, hence, it may not be advisable to disinfect this material with 2% glutaraldehyde.
MATERIALS AND METHODS: A cross-sectional comparative in vitro study was conducted. Three groups were made for testing different sterilization methods. The sample size for the study was kept as 30 observations in each of the three groups. Test samples were prepared by making an impression of the die using the putty-wash technique. Statistical analysis was done by applying unpaired t-test, paired t-test, one-way analysis of variance (ANOVA) and post hoc Tukey's honestly significant difference (HSD).
RESULTS: Initial mean of samples of group I were compared to A (actual measurement of metal ruled block = 24.960), a dimensional change of 1.6% was found. Similarly, in group II, a change of 1.59% was found and in group III the change was 1.7%. There was mean shrinkage of 24.557 mm in group I, 24.586 mm in group II, and 24.535 mm in group III and these changes were found statistically significant.
CONCLUSION: Dimensional changes in the impression material after disinfection with 2% glutaraldehyde were considered high compared to autoclaving and, hence, it may not be advisable to disinfect this material with 2% glutaraldehyde.