Volumetric change of calcium silicate-based repair materials in a simulated inflammatory environment: A micro-computed tomography study.

CONTEXT: An acidic hydrogen potential (pH) in an inflammatory condition in the periapical tissues may affect the properties of repair bioceramic cement.

AIMS: The aim of this study was to evaluate the effect of pH on the volumetric change of the ready-to-use bioceramic NeoPUTTY (NP) compared to the powder/liquid MTA Repair HP (MTAHP) after immersion in butyric acid (BA, pH 4.1) or phosphate-buffered saline (PBS, pH 7.35).

SUBJECTS AND

METHODS

Dentin tubes filled with NP or MTAHP were scanned in micro-computed tomography (micro-CT) after 24 h. Then, the specimens were immersed in 1.5 mL of BA: NP/BA, MTAHP/BA or PBS: NP/PBS, MTAHP/PBS. After 7 days, new micro-CT scans were performed. The percentage of volumetric change (extremities and internal part) of the materials was assessed.

STATISTICAL ANALYSIS USED: ANOVA/Tukey and Kruskal-Wallis tests were performed (α =0.05).

RESULTS

All materials showed a volumetric decrease after immersion in BA or PBS at the extremities in contact with the solutions. MTAHP/BA showed the highest volumetric loss. There was no difference in the volumetric change when the internal part of the materials was evaluated.

CONCLUSIONS

An acid pH negatively affects the volumetric stability of MTAHP. Low values of volumetric change were demonstrated for NP in both immersion environments.