Evaluation of the physical properties of bromelain-modified biodentine for direct pulp capping.

BACKGROUND

This study aims to evaluate the compressive strength, solubility, radiopacity, and flow of Bromelain (BR)-modified Biodentine (BD) for direct pulp capping (DPC). This is suggested to determine the impact of BR on the physical properties of BD.

METHODS

Eighty samples were prepared according to the ISO and ADA specifications and evaluated for compressive strength, solubility, radiopacity, and flow. The compressive strength was evaluated at 24 h and 21 days via a universal testing machine. The solubility was determined by weight loss after 24-hours immersion in deionized water. Radiopacity was assessed via X-ray with aluminum step-wedges, and flow was measured by the diameter of the discs under a standard weight. Independent sample t-tests were used to statistically assess the data. A significance level of 5% was considered.

RESULTS

The compressive strength was 41.08 ± 1.84 MPa for BD and 40.92 ± 1.80 MPa for BR + BD after 24 h, and 88.93 ± 3.39 MPa for BD and 87.92 ± 3.76 MPa for BR + BD after 21 days, with no significant differences. Solubility was slightly greater in the BR + BD (2.75 ± 0.10%) compared to BD (2.62 ± 0.25%), but not significantly different. The radiopacity was similar between BD (2.82 ± 0.11 mm) and BR + BD (2.73 ± 0.10 mm). BR + BD resulted in significantly greater flow (9.99 ± 0.18 mm) than did BD (9.65 ± 0.27 mm) (p ≤ 0.05).

CONCLUSION

BR-modified BD maintains BD's physical properties, with improved flow, making it a promising DPC agent that warrants further study.