Revista cientifica odontologica (Universidad Cientifica del Sur) · 2024
[Surface roughness of two composite resins after immersion in soda drinks: in vitro study].
Аннотация на английскомСтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Alarcón-Torres Sharon Gianella, Chávez-Méndez Martín Andrés
Аннотация
OBJECTIVE: Compare the surface roughness of two composite resins after immersion in carbonated beverages.
MATERIALS AND METHODS: 160 resin discs (6 x 2 mm) were divided into 8 groups (n=20 per group) according to type of resin (Filtek™ Z350 XT® and Palfique LX5®) and type of immersion in beverages (distilled water, Coca Cola®, Inca Kola® and Kola Escocesa®. The immersions were carried out under a structured cycle: 4 immersions a day for 5 days, intermediate storage in distilled water and overnight incubation for 8 h at 37°C. The measurements with the roughness meter were evaluated in three times: baseline, 7 and 14 days. The three-way Anova test was used at P<0.05.
RESULTS: Roughness showed differences only for the individual factors of time (P<0.000) and resin (P=0.000), and for the interaction time*drink (P=0.000) and resin*drink (P=0.003). Roughness was higher with Filtek Z350 XT® immersed with Inca Kola® (0.85 ± 0.37) than 14 days compared to other times (P=0.035) and with Palfique LX5 immersed in Coca Cola® at 7 days (1.61 ± 0.42) and in Inca Kola® at 14 days (1.66 ± 0.56) compared to distilled water (P<0,05).
CONCLUSION: Surface roughness was affected by the type of resin, the type of soft drink and the immersion time. The roughness was greater with the Palfique LX5® nanohybrid resin, the Inca Kola® drink and after 14 days of immersion.
MATERIALS AND METHODS: 160 resin discs (6 x 2 mm) were divided into 8 groups (n=20 per group) according to type of resin (Filtek™ Z350 XT® and Palfique LX5®) and type of immersion in beverages (distilled water, Coca Cola®, Inca Kola® and Kola Escocesa®. The immersions were carried out under a structured cycle: 4 immersions a day for 5 days, intermediate storage in distilled water and overnight incubation for 8 h at 37°C. The measurements with the roughness meter were evaluated in three times: baseline, 7 and 14 days. The three-way Anova test was used at P<0.05.
RESULTS: Roughness showed differences only for the individual factors of time (P<0.000) and resin (P=0.000), and for the interaction time*drink (P=0.000) and resin*drink (P=0.003). Roughness was higher with Filtek Z350 XT® immersed with Inca Kola® (0.85 ± 0.37) than 14 days compared to other times (P=0.035) and with Palfique LX5 immersed in Coca Cola® at 7 days (1.61 ± 0.42) and in Inca Kola® at 14 days (1.66 ± 0.56) compared to distilled water (P<0,05).
CONCLUSION: Surface roughness was affected by the type of resin, the type of soft drink and the immersion time. The roughness was greater with the Palfique LX5® nanohybrid resin, the Inca Kola® drink and after 14 days of immersion.