Effect of Zeolite Incorporation on the Ion Release Properties of Silver-Reinforced Glass Ionomer Cement.

BACKGROUND

Zeolite can release antimicrobial silver ions in a targeted and controlled manner for an extended time, selectively inhibiting the growth of pathogenic oral bacteria when added to dental materials. The objective of this study was to investigate the effect of the addition of zeolite to silver-reinforced glass ionomer cement on the release of silver ions over time.

METHODS

Five concentrations of silver-zeolite (0%, 0.5%, 1%, 2%, 4% wt) were incorporated into silver-reinforced GIC in the form of 10 mm × 2 mm circular disks (n = 5). The disks were incubated in deionized water at 37 °C and ion release from the samples was measured at 1, 2, 7, and 30 days after immersion by inductively coupled atomic emission spectroscopy.

RESULTS

Incorporating silver-zeolite increased silver ion release from silver-reinforced GIC disks compared to the control disks (p < 0.05), while incorporating zeolite alone had no effect. Higher concentrations of added silver-zeolite resulted in increased silver ion release. Sustained silver ion release was observed for up to 30 days.

CONCLUSION

Adding silver-zeolite to silver-reinforced GIC may enhance its extended antibacterial effect in the oral cavity.