Assessment of wear characteristics, longevity and stiffness of Essix-type retainers.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Alfadil Lina, Patel Mangala, Pandis Nikolaos, Fleming Padhraig S
Аннотация
OBJECTIVE: To compare four commercially available Essix-type retainers in terms of longevity, wear characteristics, stiffness and their range of rigidity.
MATERIALS AND METHODS: An in vitro study was conducted at Queen Mary University of London. Four groups of thermoplastic materials were included: Duran (PETG), Essix C + (Polypropylene), Vivera and Zendura (Polyurethane). A working typodont was fabricated to evaluate surface wear characteristics using a wear machine with a customized jig. Retainers were measured for tensile test, and water absorption was measured at five different time points up to 6 months after initial immersion in two different physical states and two different solutions. Hydrolytic degradation was also evaluated using FTIR spectroscopy.
RESULTS: Essix C + was the most flexible retainer with Vivera the stiffest material. Zendura and Essix C + had the most surface wear (413 μm ± 80 and 652 μm ± 12, respectively) with absorption rates of up to 15 wt% in artificial saliva occurring with Zendura. Only Essix C + displayed signs of degradation following water absorption.
CONCLUSIONS: All materials had characteristic levels of flexibility and were susceptible to water absorption. Duran 1.5 mm performed similarly to Vivera in relation to stiffness and wear properties. While Zendura and Vivera have similar chemical structures, they exhibited differences concerning wear resistance and water absorption. Further clinical research evaluating the clinical relevance of these laboratory findings is required.
CLINICAL RELEVANCE: Characteristic patterns of wear and rigidity of four commercially available Essix-type retainers were observed. This information should help in the tailoring of retainer material on a case-by-case basis considering treatment-related factors and patient characteristics including parafunctional habits.
MATERIALS AND METHODS: An in vitro study was conducted at Queen Mary University of London. Four groups of thermoplastic materials were included: Duran (PETG), Essix C + (Polypropylene), Vivera and Zendura (Polyurethane). A working typodont was fabricated to evaluate surface wear characteristics using a wear machine with a customized jig. Retainers were measured for tensile test, and water absorption was measured at five different time points up to 6 months after initial immersion in two different physical states and two different solutions. Hydrolytic degradation was also evaluated using FTIR spectroscopy.
RESULTS: Essix C + was the most flexible retainer with Vivera the stiffest material. Zendura and Essix C + had the most surface wear (413 μm ± 80 and 652 μm ± 12, respectively) with absorption rates of up to 15 wt% in artificial saliva occurring with Zendura. Only Essix C + displayed signs of degradation following water absorption.
CONCLUSIONS: All materials had characteristic levels of flexibility and were susceptible to water absorption. Duran 1.5 mm performed similarly to Vivera in relation to stiffness and wear properties. While Zendura and Vivera have similar chemical structures, they exhibited differences concerning wear resistance and water absorption. Further clinical research evaluating the clinical relevance of these laboratory findings is required.
CLINICAL RELEVANCE: Characteristic patterns of wear and rigidity of four commercially available Essix-type retainers were observed. This information should help in the tailoring of retainer material on a case-by-case basis considering treatment-related factors and patient characteristics including parafunctional habits.