An analysis of cyclic fatigue resistance of reciprocating instruments in different canal curvatures after immersion in sodium hypochlorite and autoclaving: An in vitro study.

AIM: The aim of this study is to assess the effect of sodium hypochlorite and sterilization on the cyclic fatigue resistance of two reciprocating nickel-titanium files using a rotary and a reciprocating motor.

MATERIALS AND

METHODS

Totally, 160 Reciproc and Wave One files were tested. The eighty files of the same brand were assigned into four groups (n = 20). These four groups were further divided into two subgroups, 1a and 1b, 2a and 2b, 3a and 3b, 4a and 4b consisting of ten files in each group. 2.5% NaOCl for 5 min, 2.5% NaOCl for 5 min + 1 cycle of autoclave sterilization, 2.5% NaOCl for 5 min + 5 cycles of autoclave sterilization, no sterilization (control). Groups 1a, 2a, 3a, and 4a were subjected to 30° and Groups 1b, 2b, 3b, and 4b were subjected to 60° canal curvature.

RESULTS

Intergroup comparison reveals that there is an increase in cyclic fatigue resistance from the first cycle to the fifth cycle of autoclave which is statistically significant.

CONCLUSION

Reciproc and Wave One showed reduced cyclic fatigue resistance on immersion in NaOCl for 5 min. Multiple autoclaving cycles significantly increased the cyclic fatigue resistance of Reciproc file system in both the curvatures. There was a decrease in cyclic fatigue resistance for Wave One after multiple autoclaving at 60° curvature which was statistically significant.