The International journal of prosthodontics · 2023
Microhardness and Gloss of a New CAD/CAM Hybrid Material Following Accelerated Aging and Coffee Immersion.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Al Amri Mohammad D, Labban Nawaf, Alhijji Saleh M, Alamri Hassan, Iskandar Mounir, Platt Jeffrey A
Аннотация
PURPOSE: To evaluate and compare the effect of accelerated aging and coffee immersion on the microhardness and gloss of a new computer-aided design and computer-aided manufacturing (CAD/CAM) hybrid material (Crystal Ultra) to those of contemporary restorative materials.
MATERIALS AND METHODS: A total of 160 specimens (12 × 14 × 1 mm ± 0.05 mm) were obtained from IPS e.max (IPS), VITA Enamic (VE), Crystal Ultra (CU), Lava Ultimate (LU), and CeraSmart (CS) high-translucency CAD/CAM blocks. The Vickers microhardness and gloss of the specimens were determined after thermocycling and coffee immersion. Data analysis was performed using SPSS (α = .05).
RESULTS: IPS and CS specimens exhibited the highest (572.66 ± 11.30) and lowest (61.92 ± 3.91) microhardness, respectively. The highest gloss was observed with IPS specimens (3.31 ± 0.32), and LU specimens showed the lowest gloss (2.33 ± 0.06). A significant difference in gloss was observed between the materials at all measurement intervals (P < .01), except at T0 (P = .43). IPS specimens showed no significant changes in either group at any measurement interval.
CONCLUSIONS: The microhardness and gloss of the new CU material were comparable to those of the tested contemporary hybrid restorative materials. Glass-ceramic showed superior hardness and gloss compared to hybrid restorative materials. Accelerated aging with thermocycling and staining significantly affected the microhardness and gloss of all tested CAD/CAM materials.
MATERIALS AND METHODS: A total of 160 specimens (12 × 14 × 1 mm ± 0.05 mm) were obtained from IPS e.max (IPS), VITA Enamic (VE), Crystal Ultra (CU), Lava Ultimate (LU), and CeraSmart (CS) high-translucency CAD/CAM blocks. The Vickers microhardness and gloss of the specimens were determined after thermocycling and coffee immersion. Data analysis was performed using SPSS (α = .05).
RESULTS: IPS and CS specimens exhibited the highest (572.66 ± 11.30) and lowest (61.92 ± 3.91) microhardness, respectively. The highest gloss was observed with IPS specimens (3.31 ± 0.32), and LU specimens showed the lowest gloss (2.33 ± 0.06). A significant difference in gloss was observed between the materials at all measurement intervals (P < .01), except at T0 (P = .43). IPS specimens showed no significant changes in either group at any measurement interval.
CONCLUSIONS: The microhardness and gloss of the new CU material were comparable to those of the tested contemporary hybrid restorative materials. Glass-ceramic showed superior hardness and gloss compared to hybrid restorative materials. Accelerated aging with thermocycling and staining significantly affected the microhardness and gloss of all tested CAD/CAM materials.