TiO2 Nanocontainers Coconstructed Using Polymers and Corrosion Inhibitors for Anticorrosion Reinforcement of Waterborne Epoxy Coatings.

Stimulus-responsive coatings can provide active corrosion protection in response to environmental changes, but they have not reached their anticipated application prospects because of the intricate preparation processes of hollow materials and methods for loading corrosion inhibitors. Herein, polyaniline molybdate corrosion inhibitor and polydopamine-wrapped titanium dioxide nanocontainers (named TiO2/PANI-MoO42-/PDA) are synthesized via a simple three-step electrostatic assembly technique. Introducing TiO2/PANI-MoO42-/PDA nanocontainers in smart waterborne epoxy (WEP) coatings affords the latter with high barriers and long-term corrosion protection. The successful deposition of each layer on the TiO2 nanocontainer surface was validated via Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy, and X-ray photoelectron spectroscopy. Release test results show that the molybdate corrosion inhibitor exhibits notable pH-responsive activity under acidic conditions and slow release in neutral environments, which improves the corrosion resistance of coatings. The addition of synthetic nanocontainers greatly improves the impermeability of WEP coatings. The charge transfer resistance of WEP/TiO2/PANI-MoO42-/PDA coatings is 1.79 × 1011 Ω cm2 after 30 day immersion in a 3.5 wt % NaCl solution, which is 3.32 × 105 times higher than that of WEP coatings. WEP/TiO2/PANI-MoO42-/PDA coatings remain uniform and reliable, even after 50 days of salt spray exposure. The excellent corrosion protection of WEP/TiO2/PANI-MoO42-/PDA coatings is attributed to (1) the enhanced dispersion and compatibility of PDA in the coating for nanocontainers, (2) the combination of phenolic hydroxyl groups of PDA and Fe, which inhibit corrosion activity on the exposed metal surface, and (3) the on-demand release of the MoO42- inhibitor, which provides sustained passivation protection. This work proposes a strategy to simplify the preparation of responsive long-term anticorrosion coatings and extend their service lives.