Demineralized dentin matrix technique - a comparison of different demineralizing solutions.

This study aimed to evaluate the microstructure formed after the chemical treatment of teeth, for the development of autogenous grafts from the demineralized dentin matrix (DDM) technique, in order to identify the most efficient demineralizing solution. The specimens, originating from the root and coronal portion, were submitted to ultrasonic cleaning and drying in an oven for 1h at 100 ºC. Then, the density was determined by Archimedes' principle for each specimen, using distilled water as immersion liquid. The samples were separated into five groups: Control group: negative control, Distilled water;EDTA group: positive control, trisodium EDTA; NaOCl group: 2.5% sodium hypochlorite; HCl-0.6M group: 0.6M hydrochloric acid; and H2O2/H2SO4 group: hydrogen peroxide and sulfuric acid. Each specimen was immersed for 1h in the corresponding group descaling solution at 60 ºC. Subsequently, the mass loss and density of the treated specimens were determined by Archimedes' principle. Ultimately, the specimens of each group were characterized by microtomography, Scanning Electron Microscopy, and Energy Dispersive Spectrometry X-ray (SEM-EDS). The results demonstrated that the H2O2/H2SO4 solution allowed the formation of interconnected micropores, suggesting better pore structures for application in scaffolds, when compared to the other studied solutions.