Development of a novel hybrid Ti6Al4V-ZrO2 surface with high wear resistance by laser and hot pressing techniques for dental implants.

The development of implant metal-free surfaces has gained attention since non-benefic results have been reported related to the metallic ions released from metal implants to the human body. Ceramic coatings have been proposed as a possible solution however, the detachment of these coatings, during implantation or even in function, can compromise its function. In order to overcome this problem, this work proposes a novel hybrid Ti6Al4V-ZrO2 surface, starting with laser texturing of the Ti6Al4V substrate by Laser Nd:YV04, followed by the allocation of the zirconia (ZrO2) powder and its subsequent sintering by hot pressing process. Results revealed that zirconia strongly adheres to titanium textured surfaces since no detachment was found under tribological and adhesion scratch tests. Moreover, the tribological results showed that the incorporation of zirconia into textured titanium surface reduces significantly the wear rate of titanium (≈93%), which is a good indicator of low metallic particles/ions released to the body. These results suggest that this novel surface with good aesthetic properties and improved wear resistance (given by zirconia) and mechanical resistance (from titanium) can be a promising solution for dental implants, especially for implant/abutment or abutment/ceramic contact zones, and thus have a huge impact on the long-term performance of implants.