Antioxidant-stabilized highly crosslinked polyethylene in total knee arthroplasty: a retrieval analysis.

AIMS: The aim of this study was to evaluate the surface damage, the density of crosslinking, and oxidation in retrieved antioxidant-stabilized highly crosslinked polyethylene (A-XLPE) tibial inserts from total knee arthroplasty (TKA), and to compare the results with a matched cohort of standard remelted highly crosslinked polyethylene (XLPE) inserts.

MATERIALS AND

METHODS

A total of 19 A-XLPE tibial inserts were retrieved during revision TKA and matched to 18 retrieved XLPE inserts according to the demographics of the patients, with a mean length of implantation of 15 months (1 to 42). The percentage areas of PE damage on the articular surfaces and the modes of damage were measured. The density of crosslinking of the PE and oxidation were measured at loaded and unloaded regions on these surfaces.

RESULTS

A-XLPE inserts had higher rates of burnishing and lower rates of pitting and scratching compared with XLPE. There were no differences in the density of crosslinking at loaded and unloaded regions. A-XLPE showed higher oxidation indices in the unloaded surface region compared with XLPE. There were no differences in the levels of oxidation in the loaded regions.

CONCLUSION

Retrieval analysis of A-XLPE did not reflect a clinically relevant difference in surface damage, density of crosslinking, or oxidation compared with XLPE tibial inserts at short-term evaluation. Cite this article: Bone Joint J 2018;100-B:1330-5.