In Situ Casting Integrated with FDM 3D Printing: Curing Behavior, Process Constraints, and Mechanical Demonstration.

Dispensing-based in situ casting offers a practical route for introducing dense or mechanically distinct polymer regions into fused deposition modeling (FDM) parts during fabrication. This study investigates the curing-dependent process constraints governing stable integration of in situ casting within an FDM workflow. In the proposed process, FDM is used to fabricate thermoplastic confinement geometries, after which liquid polymer is dispensed into selected cavities and cured before printing resumes. Two representative curing systems were examined: a UV-curable photopolymer and a two-component epoxy resin. The experimental program included UV curing characterization under perpendicular 405 nm exposure, infrared thermal imaging of curing-induced heat generation and dissipation, confined curing of epoxy resin, layer-wise integration within an FDM-printed cavity, and a representative mechanical linkage demonstration. The results show that UV-based in situ casting is constrained by the coupled effects of curing depth, peak temperature, and visible deformation, making staged curing with intermediate thermal relaxation necessary for stable operation. In contrast, the epoxy system enabled bulk cavity filling with lower peak temperature, but required substantially longer curing time, introducing a different process limitation. A layer-wise UV curing strategy enabled successful stacking of four cast layers within an FDM-printed confinement without visible leakage or shell collapse. Mechanical testing of hybrid linkage specimens further showed that localized casting can modify structural stiffness through selective reinforcement. These findings demonstrate that dispensing-based in situ casting can be integrated into FDM when thermal, temporal, and filling constraints are explicitly managed, and they provide practical process guidance for hybrid polymer fabrication involving confined casting during printing.