American journal of dentistry · 2000
Effect of stepped vs. continuous light curing exposure on bond strengths to dentin.
Клиническое исследованиеСравнительное исследованиеСтатьяРандомизированное исследованиеПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Price R B, Bannerman R A, Rizkalla A S, Hall G C
Аннотация
PURPOSE: To compare the 10-min and 24-hr shear bond strengths of three dentin bonding systems, polymerized with either a standard (Optilux 401) light for 60 s, or a stepped curing light (Elipar Highlight) that delivered a low light intensity for 10 s followed by high intensity for 50 s.
MATERIALS AND METHODS: Three bonding systems were used to bond two resin-based composites (RBC) to dentin at 34 degrees +/- 2C using the two curing lights. Single Bond (SB) and Prime & Bond 2.1 (P&B) were used with Z100 RBC, and EBS bonding system was used with Pertac II RBC. Ten specimens from each combination were debonded at 37 degrees +/- 1C 10 min after starting to light cure the bonding system. Ten other specimens were stored in water at 37 degrees +/- 1C for 24 hrs before debonding at 37 degrees +/- 1C (total 120 teeth).
RESULTS: The 10-min mean shear bond strengths were: Standard Cure; EBS 11.9 +/- 2.9 MPa, SB 14.6 +/- 2.2 MPa, P&B 14.7 +/- 4.2 MPa: Stepped Curing; EBS 7.4 +/- 2.1 MPa, SB 13.0 +/- 3.6 MPa, P&B 15.6 +/- 4.8 MPa. The 24-hr mean shear bond strengths were: Standard Cure; EBS 14.8 +/- 5.1 MPa, SB 25.1 +/- 3.3 MPa, P&B 25.2 +/- 8.8 MPa: Stepped Curing; EBS 15.1 +/- 4.6 MPa, SB 21.9 +/- 5.9 MPa, P&B 17.3 +/- 9.2 MPa. Three way ANOVA showed significant main effects for light, bonding system and time and no 2- or 3-way interaction effects at P = 0.01. The Least-Squares Means test with Sidak's adjustment for Multiple Comparisons showed that the bond strengths obtained using the standard light were significantly greater than the bond strengths obtained using the stepped curing light (P < 0.01). The 24-hr bond strengths were significantly greater (P < 0.01) than the 10-min bond strengths. The bond strengths obtained with EBS were significantly less than SB and P&B (P < 0.01), but there were no significant differences between SB and PB (P = 0.9752).
MATERIALS AND METHODS: Three bonding systems were used to bond two resin-based composites (RBC) to dentin at 34 degrees +/- 2C using the two curing lights. Single Bond (SB) and Prime & Bond 2.1 (P&B) were used with Z100 RBC, and EBS bonding system was used with Pertac II RBC. Ten specimens from each combination were debonded at 37 degrees +/- 1C 10 min after starting to light cure the bonding system. Ten other specimens were stored in water at 37 degrees +/- 1C for 24 hrs before debonding at 37 degrees +/- 1C (total 120 teeth).
RESULTS: The 10-min mean shear bond strengths were: Standard Cure; EBS 11.9 +/- 2.9 MPa, SB 14.6 +/- 2.2 MPa, P&B 14.7 +/- 4.2 MPa: Stepped Curing; EBS 7.4 +/- 2.1 MPa, SB 13.0 +/- 3.6 MPa, P&B 15.6 +/- 4.8 MPa. The 24-hr mean shear bond strengths were: Standard Cure; EBS 14.8 +/- 5.1 MPa, SB 25.1 +/- 3.3 MPa, P&B 25.2 +/- 8.8 MPa: Stepped Curing; EBS 15.1 +/- 4.6 MPa, SB 21.9 +/- 5.9 MPa, P&B 17.3 +/- 9.2 MPa. Three way ANOVA showed significant main effects for light, bonding system and time and no 2- or 3-way interaction effects at P = 0.01. The Least-Squares Means test with Sidak's adjustment for Multiple Comparisons showed that the bond strengths obtained using the standard light were significantly greater than the bond strengths obtained using the stepped curing light (P < 0.01). The 24-hr bond strengths were significantly greater (P < 0.01) than the 10-min bond strengths. The bond strengths obtained with EBS were significantly less than SB and P&B (P < 0.01), but there were no significant differences between SB and PB (P = 0.9752).
Предметные рубрики MeSH
AdhesivenessAnalysis of VarianceBisphenol A-Glycidyl MethacrylateComposite ResinsDental BondingDentinDentin-Bonding AgentsHumansLeast-Squares AnalysisLightMethacrylatesPhosphoric AcidsPolymersPolymethacrylic AcidsRadiation DosageResin CementsSilicon DioxideStatistics as TopicStress, MechanicalTemperatureTime FactorsWaterZirconium