The effect of prime-and-rinse approach using MDP micellar solutions on extrafibrillar demineralization and dentin bond performance.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Zhang Zhengyi, Zhang Yizhou, Wu Zhifang, Shi Ying, Zhou Zihuai, Wang Zhe, Jiang Wenxiang, Wang Wenting, Xu Jingqiu, Fu Baiping
Аннотация
OBJECTIVE: This study investigated the effects of prime-and-rinse approach using 10-methacryloyloxydecyl dihydrogen phosphate (MDP) micellar solutions on extrafibrillar demineralization and dentin bond performance of etch-and-rinse adhesive.
METHODS: The micellar solutions were prepared by adding 15% MDP in two ethanol-aqueous (75:25, 55:45 V/V%) solutions, referring to MDP/EtOH75 and MDP/EtOH55. After mid-coronal dentin surfaces were either etched (control) or conditioned with MDP/EtOH75 and MDP/EtOH55 and rinsed, they were applied with adhesive (Adpter Single Bond 2) in dry- or wet-bonding mode and placed with composite resin (Filtek Z350 XT). They were prepared into multiple micro-beams for micro-tensile bond strengths (MTBS) testing after storage in water for 24 h or subjecting to thermocycling. The other pretreated dentin surfaces were analyzed by TF-XRD, ATR-FTIR, HRTEM, FE-SEM, contact angle measurement and nanoindentation testing. The MTBS data was analyzed with two-way ANOVA followed by LSD post-hoc test.
RESULTS: MDP/EtOH75 produced significantly greater MTBS values than MDP/EtOH55 and control after thermocycling aging in dry- or wet-bonding mode (P < 0.05). The ATR-FTIR spectrums shows that ratios of phosphate/monomer (1,034 cm-1/1,716 cm-1) on MDP/EtOH75-, MDP/EtOH55-treated dentin surfaces are 0.51 and 0.23, respectively. This is confirmed by HRTEM images and SAED pattern that intrafibrillar minerals were mostly preserved after treatment with MDP/EtOH75. MDP/EtOH75 produced significantly higher elastic modulus and nanohardness on pretreated dentin surface than MDP/EtOH55 (P < 0.05). TF-XRD pattern shows some MDP-Ca salts remained on the primed dentin surface.
SIGNIFICANCE: Prime-and-rinse approach using MDP/EtOH75 micellar solution could produce mostly extrafibrillar demineralization, and greatly increase dentin bond durability in dry- or wet-bonding mode.
METHODS: The micellar solutions were prepared by adding 15% MDP in two ethanol-aqueous (75:25, 55:45 V/V%) solutions, referring to MDP/EtOH75 and MDP/EtOH55. After mid-coronal dentin surfaces were either etched (control) or conditioned with MDP/EtOH75 and MDP/EtOH55 and rinsed, they were applied with adhesive (Adpter Single Bond 2) in dry- or wet-bonding mode and placed with composite resin (Filtek Z350 XT). They were prepared into multiple micro-beams for micro-tensile bond strengths (MTBS) testing after storage in water for 24 h or subjecting to thermocycling. The other pretreated dentin surfaces were analyzed by TF-XRD, ATR-FTIR, HRTEM, FE-SEM, contact angle measurement and nanoindentation testing. The MTBS data was analyzed with two-way ANOVA followed by LSD post-hoc test.
RESULTS: MDP/EtOH75 produced significantly greater MTBS values than MDP/EtOH55 and control after thermocycling aging in dry- or wet-bonding mode (P < 0.05). The ATR-FTIR spectrums shows that ratios of phosphate/monomer (1,034 cm-1/1,716 cm-1) on MDP/EtOH75-, MDP/EtOH55-treated dentin surfaces are 0.51 and 0.23, respectively. This is confirmed by HRTEM images and SAED pattern that intrafibrillar minerals were mostly preserved after treatment with MDP/EtOH75. MDP/EtOH75 produced significantly higher elastic modulus and nanohardness on pretreated dentin surface than MDP/EtOH55 (P < 0.05). TF-XRD pattern shows some MDP-Ca salts remained on the primed dentin surface.
SIGNIFICANCE: Prime-and-rinse approach using MDP/EtOH75 micellar solution could produce mostly extrafibrillar demineralization, and greatly increase dentin bond durability in dry- or wet-bonding mode.