Fluoride dentifrice containing calcium silicate and sodium phosphate salts on dental erosion: In vitro study.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Leal Isabelly de Carvalho, Costa Wlhadya Kaenny De Freitas, Passos Vanara Florêncio
Аннотация
OBJECTIVE: To investigate the effect of a commercial dentifrice containing fluoride, calcium silicate, and sodium phosphate and its dual phase gel serum to prevent erosive tooth wear in enamel.
METHODS: Forty-eight enamel specimens were selected by surface hardness and randomly allocated into 4 groups (n = 12) according to the commercial toothpastes: non-fluoridated (NF); 1100 ppm Stannous fluoride (SnF2); 1450 ppm MFP + calcium silicate + sodium phosphate (CSSP); CSSP + dual-phase gel (CSSP + Serum). Cyclic experiments were repeated 3x / day for five days, including an erosive challenge with 0.05 M citric acid (pH 3.75 for 30 s), treatment with toothpaste slurries (1 min), and remineralization with artificial saliva (pH 7.0 for 60 min). Surface alterations were determined by stylus profilometry (μm) and scanning electron microscopy (SEM). Data were analyzed by ANOVA and Tukey tests (α = 0.05).
RESULTS: SnF2, CSSP and CSSP + Serum significantly reduce surface wear compared to NF treated group. Besides, there were no significant differences among SnF2, CSSP and CSSP + Serum. In micrographs of both groups treated with CSSP, the surface demonstrates the presence of a protective layer as a deposition of particles.
CONCLUSIONS: Dentifrice containing calcium silicate and sodium phosphate with or without the dual-phase gel was able to prevent the erosive tooth wear.
METHODS: Forty-eight enamel specimens were selected by surface hardness and randomly allocated into 4 groups (n = 12) according to the commercial toothpastes: non-fluoridated (NF); 1100 ppm Stannous fluoride (SnF2); 1450 ppm MFP + calcium silicate + sodium phosphate (CSSP); CSSP + dual-phase gel (CSSP + Serum). Cyclic experiments were repeated 3x / day for five days, including an erosive challenge with 0.05 M citric acid (pH 3.75 for 30 s), treatment with toothpaste slurries (1 min), and remineralization with artificial saliva (pH 7.0 for 60 min). Surface alterations were determined by stylus profilometry (μm) and scanning electron microscopy (SEM). Data were analyzed by ANOVA and Tukey tests (α = 0.05).
RESULTS: SnF2, CSSP and CSSP + Serum significantly reduce surface wear compared to NF treated group. Besides, there were no significant differences among SnF2, CSSP and CSSP + Serum. In micrographs of both groups treated with CSSP, the surface demonstrates the presence of a protective layer as a deposition of particles.
CONCLUSIONS: Dentifrice containing calcium silicate and sodium phosphate with or without the dual-phase gel was able to prevent the erosive tooth wear.