Radiopacity and cytotoxicity of Portland cement containing zirconia doped bismuth oxide radiopacifiers.
Сравнительное исследованиеСтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Chen Chiehfeng, Hsieh Sung-Chih, Teng Nai-Chia, Kao Chih-Kuo, Lee Sheng-Yang, Lin Chung-Kwei, Yang Jen-Chang
Аннотация
INTRODUCTION: This study evaluates the radiopacity and cytotoxicity of Portland cements containing a radiopacifier of bismuth oxide (Bi2O3) with yttria-stabilized zirconia (YSZ) dopant.
METHODS: Various radiopacifier powders of Bi2O3 with 0%, 15%, 30%, and 100% YSZ dopant were prepared by solid-state reaction at 700°C for 12 hours and characterized by x-ray diffraction. Portland cement/radiopacifier/calcium sulfate (75/20/5) were mixed and set by deionized water. Changes in radiopacity and in vitro cell viability of the hydrated cements were assessed. An average of 6 measured equivalent thickness of aluminum (N = 6) capable of producing similar radiographic density was recorded. The cytotoxicity of each material was determined in MC3T3 E1 cell-based methyl-thiazol-tetrazolium assay.
RESULTS: The x-ray diffraction patterns of YSZ doped Bi2O3 are different from those of pure Bi2O3 and YSZ. The cement-containing radiopacifier of Bi2O3/YSZ (85/15) presented significantly greater radiopacity (P < .05) compared with pure Bi2O3. The mouse osteoblastic cell (MC3T3-E1) viabilities of these 2 groups were statistically similar (P < .05).
CONCLUSIONS: The radiopacifier of Bi2O3/YSZ (85/15) reveals higher radiopacity but similar cell viability when compared with pure Bi2O3. It shows potential use as an alternative radiopacifier in root-end filling materials.
METHODS: Various radiopacifier powders of Bi2O3 with 0%, 15%, 30%, and 100% YSZ dopant were prepared by solid-state reaction at 700°C for 12 hours and characterized by x-ray diffraction. Portland cement/radiopacifier/calcium sulfate (75/20/5) were mixed and set by deionized water. Changes in radiopacity and in vitro cell viability of the hydrated cements were assessed. An average of 6 measured equivalent thickness of aluminum (N = 6) capable of producing similar radiographic density was recorded. The cytotoxicity of each material was determined in MC3T3 E1 cell-based methyl-thiazol-tetrazolium assay.
RESULTS: The x-ray diffraction patterns of YSZ doped Bi2O3 are different from those of pure Bi2O3 and YSZ. The cement-containing radiopacifier of Bi2O3/YSZ (85/15) presented significantly greater radiopacity (P < .05) compared with pure Bi2O3. The mouse osteoblastic cell (MC3T3-E1) viabilities of these 2 groups were statistically similar (P < .05).
CONCLUSIONS: The radiopacifier of Bi2O3/YSZ (85/15) reveals higher radiopacity but similar cell viability when compared with pure Bi2O3. It shows potential use as an alternative radiopacifier in root-end filling materials.
Предметные рубрики MeSH
3T3 CellsAluminum CompoundsAnimalsBiocompatible MaterialsBismuthCalcium CompoundsCalcium SulfateCell SurvivalCeramicsColoring AgentsContrast MediaDrug CombinationsHot TemperatureMaterials TestingMiceOsteoblastsOxidesRoot Canal Filling MaterialsSilicatesTetrazolium SaltsThiazolesTime FactorsX-Ray DiffractionYttriumZirconium