Dental materials : official publication of the Academy of Dental Materials · 2013
Adhesive interfacial interaction affected by different carbon-chain monomers.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Yoshihara Kumiko, Yoshida Yasuhiro, Nagaoka Noriyuki, Hayakawa Satoshi, Okihara Takumi, De Munck Jan, Maruo Yukinori, Nishigawa Goro, Minagi Shogo, Osaka Akiyoshi, Van Meerbeek Bart
Аннотация
OBJECTIVES: The functional monomer 10-methacryloxydecyl dihydrogen phosphate (10-MDP), recently used in more self-etch adhesives, chemically bonds to hydroxyapatite (HAp) and thus tooth tissue. Although the interfacial interaction of the phosphoric-acid functional group of 10-MDP with HAp-based substrates has well been documented, the effect of the long carbon-chain spacer of 10-MDP on the bonding effectiveness is far from understood.
METHODS: We investigated three phosphoric-acid monomers, 2-methacryloyloxyethyl dihydrogen phosphate (2-MEP), 6-methacryloyloxyhexyl dihydrogen phosphate (6-MHP) and 10-MDP, that only differed for the length of the carbon chain, on their chemical interaction potential with HAp and dentin, this correlatively using X-ray diffraction (XRD) and transmission electron microscopy (TEM). Commercial 6-MHP and 10-MDP containing adhesives were investigated as well.
RESULTS: XRD revealed that on HAp only 10-MDP produced monomer-calcium salts in the form of 'nano-layering', while on dentin all monomers produced 'nano-layering', but with a varying intensity in the order of 10-MDP>6-MHP>2-MEP. TEM confirmed that 10-MDP formed the thickest hybrid and adhesive layer. XRD and TEM revealed 'nano-layering' for all commercial adhesives on dentin, though less intensively for the 6-MHP containing adhesive than for the 10-MDP ones.
SIGNIFICANCE: It is concluded that not only the phosphoric-acid group but also the spacer group, and its length, affect the chemical interaction potential with HAp and dentin. In addition, the relatively strong 'etching' effect of 10-MDP forms more stable monomer-Ca salts, or 'nano-layering', than the two shorter carbon-chain monomers tested, thereby explaining, at least in part, the better bond durability documented with 10-MDP containing adhesives.
METHODS: We investigated three phosphoric-acid monomers, 2-methacryloyloxyethyl dihydrogen phosphate (2-MEP), 6-methacryloyloxyhexyl dihydrogen phosphate (6-MHP) and 10-MDP, that only differed for the length of the carbon chain, on their chemical interaction potential with HAp and dentin, this correlatively using X-ray diffraction (XRD) and transmission electron microscopy (TEM). Commercial 6-MHP and 10-MDP containing adhesives were investigated as well.
RESULTS: XRD revealed that on HAp only 10-MDP produced monomer-calcium salts in the form of 'nano-layering', while on dentin all monomers produced 'nano-layering', but with a varying intensity in the order of 10-MDP>6-MHP>2-MEP. TEM confirmed that 10-MDP formed the thickest hybrid and adhesive layer. XRD and TEM revealed 'nano-layering' for all commercial adhesives on dentin, though less intensively for the 6-MHP containing adhesive than for the 10-MDP ones.
SIGNIFICANCE: It is concluded that not only the phosphoric-acid group but also the spacer group, and its length, affect the chemical interaction potential with HAp and dentin. In addition, the relatively strong 'etching' effect of 10-MDP forms more stable monomer-Ca salts, or 'nano-layering', than the two shorter carbon-chain monomers tested, thereby explaining, at least in part, the better bond durability documented with 10-MDP containing adhesives.