Comparative Study of 3-Dimensional-Printed Poly-L-Lactic Acid/Bone Morphogenetic Protein (BMP)/Collagen Bone Substitute and Commercial Hydroxyapatite/BMP for Bone Regeneration Efficacy Using a Mouse Calvarial Model.
СтатьяСравнительное исследованиеНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Kim Tae Ho, Hong Yu Ri, Lim Jeong Ok, Oh Chang-Wug
Аннотация
BACKGROUND: Bone substitutes such as hydroxyapatite (HA) ceramic and recombinant bone morphogenetic protein-2 (BMP-2) are essential in treating bone defects. However, the challenges of controlled and localized BMP-2 delivery necessitate the development of advanced bone graft substitutes. This study introduces and evaluates an innovative, ready-to-use bone substitute employing 3-dimensional-printed poly-L-lactic acid (PLLA) scaffolds combined with BMP-2 to enhance bone regeneration efficiency.
METHODS: We conducted a comparative study using C57BL/6 mice to evaluate the efficacy of rhBMP-2-coated PLLA scaffolds against traditional HA-based bone graft materials. The PLLA scaffolds were coated with varying concentrations of BMP-2 using an alginate-catechol method. Bone regeneration was assessed through micro-computed tomography (CT) imaging and histological analysis 4 weeks after implantation. The statistical significance of bone mass and formation differences across groups was determined using Student t-test and analysis of variance.
RESULTS: Micro-CT analysis revealed substantial bone formation in the group with PLLA scaffolds containing 0.1% BMP-2, exhibiting a bone volume ratio of 11.1% ± 2.8%, significantly higher than all other groups (p = 0.008). Histological analysis corroborated these findings, showing dense collagen deposition and active osteoblast presence in this group, indicating enhanced bone regeneration.
CONCLUSIONS: The novel PLLA scaffold with alginate-catechol-coated BMP-2 significantly enhances bone regeneration compared to traditional bone graft materials. This innovative approach holds promising potential for clinical applications in orthopedics, particularly for treating bone defects.
METHODS: We conducted a comparative study using C57BL/6 mice to evaluate the efficacy of rhBMP-2-coated PLLA scaffolds against traditional HA-based bone graft materials. The PLLA scaffolds were coated with varying concentrations of BMP-2 using an alginate-catechol method. Bone regeneration was assessed through micro-computed tomography (CT) imaging and histological analysis 4 weeks after implantation. The statistical significance of bone mass and formation differences across groups was determined using Student t-test and analysis of variance.
RESULTS: Micro-CT analysis revealed substantial bone formation in the group with PLLA scaffolds containing 0.1% BMP-2, exhibiting a bone volume ratio of 11.1% ± 2.8%, significantly higher than all other groups (p = 0.008). Histological analysis corroborated these findings, showing dense collagen deposition and active osteoblast presence in this group, indicating enhanced bone regeneration.
CONCLUSIONS: The novel PLLA scaffold with alginate-catechol-coated BMP-2 significantly enhances bone regeneration compared to traditional bone graft materials. This innovative approach holds promising potential for clinical applications in orthopedics, particularly for treating bone defects.