Electrochemical deposition of lithium coating on titanium implant with enhanced early stage osseointegration.

Recently, a large number of studies have reported that lithium (Li) displayed a positive effect on osteogenesis. However, only a few studies have investigated the Li-incorporated surfaces through electrochemical deposition. In this study, electrochemical deposition was conducted on a CHI600E electrochemical workstation. The characterization of electrochemical deposition (ECD) and ECD-Li surfaces were detected by field-emission scanning electron microscopy with energy-dispersive spectrometer. rBMSCs were cultured on two surfaces for subsequent adhesion, proliferation and live/dead assay. To evaluate the effects of Li-incorporated implants by electrochemical deposition on osseointegration in vivo, teeth extraction of two premolars and one first molar in bilateral mandible were performed on six male beagle dogs. After 3 months, ZDI and ZDI-Li implants were inserted into the bilateral mandible of each beagle dog. Micro Computed Tomography (Micro-CT) and hard tissue sectioning analysis were carried out to evaluate the osseointegration at 4- and 8-weeks post-implantation. Results showed that ECD-Li surface promoted adhesion and proliferation of BMSCs in the early stage. More importantly, through micro-CT analysis, the values of bone volume/total volume (BV/TV) (0.374 ± 0.015), bone-implant contact (BIC) (0.831 ± 0.025), and Tb.Th (0.412 ± 0.007) in ZDI-Li group was significantly higher than those of ZDI group (0.302 ± 0.009, 0.700 ± 0.023, 0.353 ± 0.001, p < .01) at 4 weeks. Similarly, ZDI-Li group manifested more bone contact with the implant surfaces at 4 weeks based on hard tissue sectioning analysis, whereas no significant difference was detected between two groups at 8 weeks. Therefore, incorporating Li into implant surface through ECD could enhance early osseointegration in vivo.