Oral health & preventive dentistry · 2019
Remineralising Effectiveness of Two Fluoride Varnishes Containing Additives: An In Vitro Study.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Jain Avani, Suprabha Baranya Shrikrishna, Shenoy Ramya, Natarajan Srikant, Rao Arathi
Аннотация
PURPOSE: To assess the remineralising efficacy of fluoride varnish containing additives and conventional sodium fluoride varnish.
MATERIALS AND METHODS: 72 extracted upper central incisors specimens were randomly allocated to four groups after demineralisation: control; 5% sodium fluoride varnish (FV) (Fluoritop-SR); resin modified glass ionomer-based calcium phosphate containing fluoride varnish (CV) (Clinpro XT); fluoride varnish with xylitol coated calcium phosphate (cXp) (Embrace). Change in surface morphology, calcium phosphorous ratio and fluoride content of enamel were evaluated using scanning electron microscope and energy dispersive X-ray analysis (SEM-EDAX). Change in surface roughness was evaluated using profilometer analysis. All readings were taken at baseline, after demineralisation, at 2 weeks and 4 weeks of remineralisation.
RESULTS: At 4 weeks of remineralisation surface roughness values were ranked as follows: control > FV = cXp > CV. Calcium phosphorus ratios were in the order: CV > FV = cXp > control and fluoride content (for treatment groups): CV = cXp > FV. Scanning electron microscopy images showed mineral deposition on the surfaces of the treatment groups with different deposition pattern of minerals.
CONCLUSION: Fluoride varnishes with or without additives are effective in remineralisation of early enamel lesions. Glass ionomer-based fluoride varnish results in better remineralisation than xylitol coated calcium phosphate containing fluoride varnish and 5% sodium fluoride varnish.
MATERIALS AND METHODS: 72 extracted upper central incisors specimens were randomly allocated to four groups after demineralisation: control; 5% sodium fluoride varnish (FV) (Fluoritop-SR); resin modified glass ionomer-based calcium phosphate containing fluoride varnish (CV) (Clinpro XT); fluoride varnish with xylitol coated calcium phosphate (cXp) (Embrace). Change in surface morphology, calcium phosphorous ratio and fluoride content of enamel were evaluated using scanning electron microscope and energy dispersive X-ray analysis (SEM-EDAX). Change in surface roughness was evaluated using profilometer analysis. All readings were taken at baseline, after demineralisation, at 2 weeks and 4 weeks of remineralisation.
RESULTS: At 4 weeks of remineralisation surface roughness values were ranked as follows: control > FV = cXp > CV. Calcium phosphorus ratios were in the order: CV > FV = cXp > control and fluoride content (for treatment groups): CV = cXp > FV. Scanning electron microscopy images showed mineral deposition on the surfaces of the treatment groups with different deposition pattern of minerals.
CONCLUSION: Fluoride varnishes with or without additives are effective in remineralisation of early enamel lesions. Glass ionomer-based fluoride varnish results in better remineralisation than xylitol coated calcium phosphate containing fluoride varnish and 5% sodium fluoride varnish.