Biomimetic remineralization of acid etched enamel using agarose hydrogel model.

Background

Minimally invasive dentistry aims to prevent progression of caries and treats non-cavitated lesions through non-invasive approaches to preserve the integrity of tooth structure. The aim of this research was to investigate the possible biomimetic effect of agarose hydrogel in remineralizing a human demineralized enamel model.

Methods

Mandibular third molars were distributed into three groups (G1, G2 and G3) according to the follow up time (2, 4 and 6 days respectively). Caries like lesion was prepared by applying 37% phosphoric acid gel for 1 minute and then remineralization was performed through applying agarose hydrogel on the demineralized surfaces. The specimens were placed in phosphate solution at 37˚C for 2, 4 & 6 days. Scanning electron microscope (SEM), surface microhardness (SMH) and surface roughness analysis (SR) were performed to assess the regenerated tissue.

Results

SEM revealed mineral depositions on the demineralized enamel surface that increased in density by time resulting in a relatively smooth surface in G3. SR and SMH analysis revealed significant differences between the remineralized enamel surfaces of different groups (p< 0.00001) with the highest SR in G1 and the highest SMH in G3.

Conclusions

Agarose hydrogel application is a promising approach to treat early carious lesion. Further studies are needed to clarify the stability of agarose hydrogels in clinical application.