Operative dentistry · 2015
Bleaching Effects on Color, Chemical, and Mechanical Properties of White Spot Lesions.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Kim Y, Son H H, Yi K, Ahn J S, Chang J
Аннотация
OBJECTIVE: The purpose of the study was to evaluate the effect of bleaching on teeth with white spot lesions.
METHODS AND MATERIALS: Carious lesions with standardized whiteness were produced on the buccal and lingual surfaces of human premolars by pH cycling. Specimens were subjected to four experimental conditions (n=20/group) as follows: group 1, control; group 2, caries formation followed by remineralization using fluoride-containing casein phosphopeptide-amorphous calcium phosphate (CPP-ACP; Tooth Mousse Plus, GC, Tokyo, Japan); group 3, caries formation followed by bleaching using 10% carbamide peroxide; and group 4, caries formation followed by both bleaching and remineralization. The CIE L(*)a(*)b(*) color values were measured with a spectroradiometer, the mineral content was measured with electron probe microanalysis (EPMA) on the cross-sectional surface of each specimen, and the Knoop hardness test was carried out along the EPMA scan line. Two-way analysis of variance was performed with Tukey post hoc comparison.
RESULTS: The change in the CIE color values was not significantly different between the caries-formed (ΔE(*)=7.03) and the bleached enamel (ΔE(*)=7.60). Bleaching of the carious enamel extended the whiteness (ΔE(*)=3.38) without additional mineral loss (p<0.05). The remineralization treatment significantly increased the calcium (Ca), phosphate (P), and fluoride content of the subsurface lesion area (p<0.05). The cross-sectional microhardness values correlated well with the Ca and P content (R>0.80).
CONCLUSIONS: Bleaching reduced the color disparities between sound and carious enamel without deteriorating the chemical and mechanical properties. The application of CPP-ACP paste enhanced mineral deposition in the subsurface lesion area of carious enamel.
METHODS AND MATERIALS: Carious lesions with standardized whiteness were produced on the buccal and lingual surfaces of human premolars by pH cycling. Specimens were subjected to four experimental conditions (n=20/group) as follows: group 1, control; group 2, caries formation followed by remineralization using fluoride-containing casein phosphopeptide-amorphous calcium phosphate (CPP-ACP; Tooth Mousse Plus, GC, Tokyo, Japan); group 3, caries formation followed by bleaching using 10% carbamide peroxide; and group 4, caries formation followed by both bleaching and remineralization. The CIE L(*)a(*)b(*) color values were measured with a spectroradiometer, the mineral content was measured with electron probe microanalysis (EPMA) on the cross-sectional surface of each specimen, and the Knoop hardness test was carried out along the EPMA scan line. Two-way analysis of variance was performed with Tukey post hoc comparison.
RESULTS: The change in the CIE color values was not significantly different between the caries-formed (ΔE(*)=7.03) and the bleached enamel (ΔE(*)=7.60). Bleaching of the carious enamel extended the whiteness (ΔE(*)=3.38) without additional mineral loss (p<0.05). The remineralization treatment significantly increased the calcium (Ca), phosphate (P), and fluoride content of the subsurface lesion area (p<0.05). The cross-sectional microhardness values correlated well with the Ca and P content (R>0.80).
CONCLUSIONS: Bleaching reduced the color disparities between sound and carious enamel without deteriorating the chemical and mechanical properties. The application of CPP-ACP paste enhanced mineral deposition in the subsurface lesion area of carious enamel.