Crestal bone loss associated with different implant surfaces in the posterior mandible in patients with a history of periodontitis. A retrospective study.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Sicilia Alberto, Gallego Luis, Sicilia Pelayo, Mallo Carmen, Cuesta Susana, Sanz Mariano
Аннотация
OBJECTIVE: To retrospectively assess the interproximal bone loss (CBL) in external hexagon implants (EHI), with different surface micro-topography, placed in the posterior mandible in patients with a history of periodontitis undergoing supportive periodontal care.
MATERIAL AND METHODS: 268 consecutive patients received 755 EHI implants in the mandibular molar region between 2007 and 2015 with the following surface characteristics: 72 turned, 145 hybrids (double acid-etched/turned), and 538 anodized. CBL was yearly evaluated by analysing calibrated digital periapical radiographs, with a follow-up of 1-6 years. Data on implant survival were also calculated.
RESULTS: At 6 years (53 patients), the mean CBL was 1.34/1.42 mm at patient/implant level, respectively (range: 0-5.2 mm). Significantly higher CBL was detected in anodized implants than in turned and hybrid implants (1.92/1.46/1.02 mm) (p < .01). The maximum CBL values were found in 2 anodized implants at 4 years (6.3 and 8.1 mm). CBL ≥2 mm was detected in 18% of implants at 3 years and 35% at 6 (p < 2.2 × 10-16 ), this prevalence being 2.6 times higher in the anodized than in the hybrid and turned group (40%/15.6%, p < .0094). At 6 years, 25 anodized implants presented CBL ≥3 mm (18%). 6 anodized implants (5 patients) were removed between 4 and 5 years.
CONCLUSION: A significant higher CBL was observed in anodized, compared to hybrid and turned implants, when placed in the mandibular molar region of periodontal patients, with a follow-up of 1 to 6 years.
MATERIAL AND METHODS: 268 consecutive patients received 755 EHI implants in the mandibular molar region between 2007 and 2015 with the following surface characteristics: 72 turned, 145 hybrids (double acid-etched/turned), and 538 anodized. CBL was yearly evaluated by analysing calibrated digital periapical radiographs, with a follow-up of 1-6 years. Data on implant survival were also calculated.
RESULTS: At 6 years (53 patients), the mean CBL was 1.34/1.42 mm at patient/implant level, respectively (range: 0-5.2 mm). Significantly higher CBL was detected in anodized implants than in turned and hybrid implants (1.92/1.46/1.02 mm) (p < .01). The maximum CBL values were found in 2 anodized implants at 4 years (6.3 and 8.1 mm). CBL ≥2 mm was detected in 18% of implants at 3 years and 35% at 6 (p < 2.2 × 10-16 ), this prevalence being 2.6 times higher in the anodized than in the hybrid and turned group (40%/15.6%, p < .0094). At 6 years, 25 anodized implants presented CBL ≥3 mm (18%). 6 anodized implants (5 patients) were removed between 4 and 5 years.
CONCLUSION: A significant higher CBL was observed in anodized, compared to hybrid and turned implants, when placed in the mandibular molar region of periodontal patients, with a follow-up of 1 to 6 years.