Timing of bioprosthetic valve fracture in transcatheter valve-in-valve intervention: impact on valve durability and leaflet integrity.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Meier David, Payne Geoffrey W, Mostaço-Guidolin Leila B, Bouchareb Rihab, Rich Courtney, Lai Althea, Chatfield Andrew G, Akodad Mariama, Salcudean Hannah, Lutter Georg, Puehler Thomas, Pibarot Philippe, Allen Keith B, Chhatriwalla Adnan K, Sondergaard Lars, Wood David A, Webb John G, Leipsic Jonathon A, Sathananthan Janarthanan, Sellers Stephanie L
Аннотация
BACKGROUND: Bioprosthetic valve fracture (BVF) can be used to improve transcatheter heart valve (THV) haemodynamics following a valve-in-valve (ViV) intervention. However, whether BVF should be performed before or after THV deployment and the implications on durability are unknown. Aims: We sought to assess the impact of BVF timing on long-term THV durability.
METHODS: The impact of BVF timing was assessed using small ACURATE neo (ACn) or 23 mm SAPIEN 3 (S3) THV deployed in 21 mm Mitroflow valves compared to no-BVF controls. Valves underwent accelerated wear testing up to 200 million (M) cycles (equivalent to 5 years). At 200M cycles, THV were evaluated by hydrodynamic testing, second-harmonic generation (SHG) microscopy, scanning electron microscopy (SEM) and histology.
RESULTS: At 200M cycles, the regurgitant fraction (RF) and effective orifice area (EOA) for the ACn were 8.03±0.30%/1.74±0.01 cm2 (no BVF), 12.48±0.70%/1.97±0.02 cm2 (BVF before ViV) and 9.29±0.38%/2.21±0.0 cm2 (BVF after ViV), respectively. For the S3 these values were 2.63±0.51%/1.26±0.01 cm2, 2.03±0.42%/1.65±0.01 cm2, and 1.62±0.38%/2.22±0.01 cm2, respectively. Further, SHG and SEM revealed a higher degree of superficial leaflet damage when BVF was performed after ViV for the ACn and S3. However, the histological analysis revealed significantly less damage, as determined by matrix density analysis, through the entire leaflet thickness when BVF was performed after ViV with the S3 and a similar but non-significant trend with the ACn. Conclusions: BVF performed after ViV appears to offer superior long-term EOA without increased RF. Ultrastructure leaflet analysis reveals that the timing of BVF can differentially impact leaflets, with more superficial damage but greater preservation of overall leaflet structure when BVF is performed after ViV.
METHODS: The impact of BVF timing was assessed using small ACURATE neo (ACn) or 23 mm SAPIEN 3 (S3) THV deployed in 21 mm Mitroflow valves compared to no-BVF controls. Valves underwent accelerated wear testing up to 200 million (M) cycles (equivalent to 5 years). At 200M cycles, THV were evaluated by hydrodynamic testing, second-harmonic generation (SHG) microscopy, scanning electron microscopy (SEM) and histology.
RESULTS: At 200M cycles, the regurgitant fraction (RF) and effective orifice area (EOA) for the ACn were 8.03±0.30%/1.74±0.01 cm2 (no BVF), 12.48±0.70%/1.97±0.02 cm2 (BVF before ViV) and 9.29±0.38%/2.21±0.0 cm2 (BVF after ViV), respectively. For the S3 these values were 2.63±0.51%/1.26±0.01 cm2, 2.03±0.42%/1.65±0.01 cm2, and 1.62±0.38%/2.22±0.01 cm2, respectively. Further, SHG and SEM revealed a higher degree of superficial leaflet damage when BVF was performed after ViV for the ACn and S3. However, the histological analysis revealed significantly less damage, as determined by matrix density analysis, through the entire leaflet thickness when BVF was performed after ViV with the S3 and a similar but non-significant trend with the ACn. Conclusions: BVF performed after ViV appears to offer superior long-term EOA without increased RF. Ultrastructure leaflet analysis reveals that the timing of BVF can differentially impact leaflets, with more superficial damage but greater preservation of overall leaflet structure when BVF is performed after ViV.