Evaluation of optical, surface, and microbiological properties of computer-aided design/computer-aided manufacturing-milled and three-dimensional-printed denture bases after aging by thermocycling: An in vitro study.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Bento Victor Augusto Alves, Sayeg João Mateus Cavalaro, Rosa Cleber Davi Del Rei Daltro, Lopes Leonardo Ferreira de Toledo Piza, Marques Maria Carolina Silva, Pellizzer Eduardo Piza
Аннотация
AIM: The purpose of this study was to evaluate the surface properties, optical stability, and Candida albicans adhesion to resins used in the base of conventional, milled, and three-dimensional (3D)-printed dentures after aging by thermocycling.
SETTINGS AND DESIGN: In vitro study.
MATERIALS AND METHODS: A total of 96 resin samples were manufactured, divided into 3 resin groups (n= 32) (conventional thermally activated, milled and 3D-printed), and subdivided into 4 aging times by thermocycling at temperatures 5 ± 1°C and 55 ± 1°C in 24h, 5.000, 10.000, 20.000 cycles (n = 8), evaluating the adhesion of C. albicans, optical stability, surface roughness, hydrophilicity, and energy surface.
STATISTICAL ANALYSIS USED: Data were evaluated by two-way ANOVA and Tukey's test for pairwise comparisons (P < .05).
RESULTS: Conventional resin exhibited lower C. albicans colonization, with significant reductions at T1 (1.05±1.38) (P = .003) and T3 (3.67 ±1.86) (P = .023) compared to other resins. The conventional resin had significantly the lowest ΔE00 value at T0 (0.98 ± 0.41) (P < .05). The milled resin had significantly lower roughness value at T0 (0.031 ± 0.00) (P < .05). The conventional resin had significantly higher surface energy values compared to the other resins (P < .05). The conventional resin exhibited a significantly lower water contact angle than the other resins (P < .001).
CONCLUSION: The conventional thermally activated resin showed less adhesion of C. albicans than the resins manufactured by CAD/CAM. Among CAD/CAM resins, milled resin showed better properties than 3D-printed resin over time.
SETTINGS AND DESIGN: In vitro study.
MATERIALS AND METHODS: A total of 96 resin samples were manufactured, divided into 3 resin groups (n= 32) (conventional thermally activated, milled and 3D-printed), and subdivided into 4 aging times by thermocycling at temperatures 5 ± 1°C and 55 ± 1°C in 24h, 5.000, 10.000, 20.000 cycles (n = 8), evaluating the adhesion of C. albicans, optical stability, surface roughness, hydrophilicity, and energy surface.
STATISTICAL ANALYSIS USED: Data were evaluated by two-way ANOVA and Tukey's test for pairwise comparisons (P < .05).
RESULTS: Conventional resin exhibited lower C. albicans colonization, with significant reductions at T1 (1.05±1.38) (P = .003) and T3 (3.67 ±1.86) (P = .023) compared to other resins. The conventional resin had significantly the lowest ΔE00 value at T0 (0.98 ± 0.41) (P < .05). The milled resin had significantly lower roughness value at T0 (0.031 ± 0.00) (P < .05). The conventional resin had significantly higher surface energy values compared to the other resins (P < .05). The conventional resin exhibited a significantly lower water contact angle than the other resins (P < .001).
CONCLUSION: The conventional thermally activated resin showed less adhesion of C. albicans than the resins manufactured by CAD/CAM. Among CAD/CAM resins, milled resin showed better properties than 3D-printed resin over time.