The effect of collagen cross-linking procedure on the material of intracorneal ring segments.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Sideroudi Haris, Labiris Georgios, Soto-Beobide Amaia, Voyiatzis Georgios, Chrissanthopoulos Athanassios, Kozobolis Vassilios
Аннотация
PURPOSE: To assess the potential impact of corneal crosslinking treatment (365 nm ultraviolet (UV)A irradiation with riboflavin) on the material properties of Intracorneal Rings Segments (ICRS).
MATERIALS AND METHODS: Material properties were studied using FT-IR spectroscopy and UV-Vis spectroscopy. Rings were examined: (1) after installation of riboflavin solution, (2) after irradiation with UV-A light and (3) after instillation of riboflavin solution followed by instillation and coeval irradiation. The experiments followed the standard corneal cross-linking (CXL) protocol of corneal crosslinking treatment.
RESULTS: After instillation of riboflavin solution, a permanent intense yellow staining of the samples was observed. UV-Vis spectroscopy confirmed that a certain amount of riboflavin solution was absorbed into the samples after CXL procedure. FT-IR spectroscopic analysis showed alterations in the spectra of ICRS mainly at the 2800-3200 cm(-1) spectral region [modification in band intensities of CH(2) (2925 cm(-1)) and CH(3) (2950 cm(-1))].
CONCLUSIONS: Our results suggest crosslinking reaction in ICRS material. This should be taken into consideration prior to any CXL treatment of post ICRS-implanted cornea.
MATERIALS AND METHODS: Material properties were studied using FT-IR spectroscopy and UV-Vis spectroscopy. Rings were examined: (1) after installation of riboflavin solution, (2) after irradiation with UV-A light and (3) after instillation of riboflavin solution followed by instillation and coeval irradiation. The experiments followed the standard corneal cross-linking (CXL) protocol of corneal crosslinking treatment.
RESULTS: After instillation of riboflavin solution, a permanent intense yellow staining of the samples was observed. UV-Vis spectroscopy confirmed that a certain amount of riboflavin solution was absorbed into the samples after CXL procedure. FT-IR spectroscopic analysis showed alterations in the spectra of ICRS mainly at the 2800-3200 cm(-1) spectral region [modification in band intensities of CH(2) (2925 cm(-1)) and CH(3) (2950 cm(-1))].
CONCLUSIONS: Our results suggest crosslinking reaction in ICRS material. This should be taken into consideration prior to any CXL treatment of post ICRS-implanted cornea.