Staining of dentin from amalgam corrosion is induced by demineralization.
Сравнительное исследованиеСтатьяРандомизированное исследованиеНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Scholtanus Johannes D, van der Hoorn Wietske, Ozcan Mutlu, Huysmans Marie-Charlotte D N J M, Roeters Joost F M, Kleverlaan Cornelis J, Feilzer Albert J
Аннотация
PURPOSE: To evaluate the effect of artificial demineralization upon color change of dentin in contact with dental amalgam.
METHODS: Sound human molars (n = 34) were embedded in resin and coronal enamel was removed. Dentin was exposed to artificial caries gel (pH 5.5) at 37 degrees C for 12 weeks (n = 24). Non-demineralized teeth served as controls (n = the 10). A dispersive high-Cu amalgam or conventional low-Cu amalgam was condensed onto dentin surfaces of all groups. After 10 weeks storage in saline, amalgam was removed and teeth were cut into three slices. Surfaces were inspected under optical microscopy and photographed.
RESULTS: Penetration of black pigments was observed in dentin underneath both high-Cu and low-Cu amalgams in demineralized specimens. Black deposits were unevenly distributed and observed predominantly in dentin near to pulp horns. Discoloration was not limited to outer demineralized dentin but extended beyond this zone. Evenly distributed bluish-green discoloration was observed underneath all high-Cu amalgam specimens independent of demineralization.
METHODS: Sound human molars (n = 34) were embedded in resin and coronal enamel was removed. Dentin was exposed to artificial caries gel (pH 5.5) at 37 degrees C for 12 weeks (n = 24). Non-demineralized teeth served as controls (n = the 10). A dispersive high-Cu amalgam or conventional low-Cu amalgam was condensed onto dentin surfaces of all groups. After 10 weeks storage in saline, amalgam was removed and teeth were cut into three slices. Surfaces were inspected under optical microscopy and photographed.
RESULTS: Penetration of black pigments was observed in dentin underneath both high-Cu and low-Cu amalgams in demineralized specimens. Black deposits were unevenly distributed and observed predominantly in dentin near to pulp horns. Discoloration was not limited to outer demineralized dentin but extended beyond this zone. Evenly distributed bluish-green discoloration was observed underneath all high-Cu amalgam specimens independent of demineralization.