The journal of adhesive dentistry · 2012
Effects of a peripheral enamel margin on the long-term bond strength and nanoleakage of composite/dentin interfaces produced by self-adhesive and conventional resin cements.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Kasaz Alline C, Pena Carlos E, de Alexandre Rodrigo S, Viotti Ronaldo G, Santana Veronica B, Arrais Cesar A G, Giannini Marcelo, Reis Andre F
Аннотация
PURPOSE: This study evaluated the effects of peripheral enamel margins on the long-term bond strength (µTBS) and nanoleakage in resin/dentin interfaces produced by self-adhesive and conventional resin cements.
MATERIALS AND METHODS: Five self-adhesive [RelyX-Unicem (UN), RelyX-U100 (UC), GCem (GC), Maxcem (MC), Set (SET)] and 2 conventional resin cements [RelyX-ARC(RX), Panavia F(PF)] were used. An additional group included the use of a two-step self-etching adhesive (SE Bond) with Panavia F (PS). One hundred ninety-two molars were assigned to 8 groups according to luting material. Five-mm-thick composite disks were cemented and assigned to 3 subgroups according to water-exposure condition (n = 6): 24-h peripheral exposure (24h-PE-enamel margins), or 1 year of peripheral (1 yr-PE) or direct exposure (1 yr-DE-dentin margin). Restored teeth were sectioned into beams and tested in tension at 1 mm/min. Data were analyzed by two-way ANOVA and Tukey's test. Two additional specimens in each group were prepared for nanoleakage evaluation. Nanoleakage patterns were observed under SEM/TEM.
RESULTS: Except for RX, no significant reduction in µTBS was observed between 24h-PE and 1 yr-PE. 1 yr-DE reduced µTBS for RX, PF, GC, MC, and SET. No significant reduction in µTBS was observed for PS, UC, and UN after 1 year. After 1 yr-DE, RX and PS presented the highest µTBS, and SET and MC the lowest. Nanoleakage was reduced when there was a peripheral enamel margin. SET and MC presented more silver deposition than other groups.
CONCLUSION: The presence of a peripheral enamel margin reduced the degradation rate in resin/dentin interfaces for most materials. The µTBS values produced by the multi-step luting agents RX and PS were significantly higher than those observed for self-adhesive cement.
MATERIALS AND METHODS: Five self-adhesive [RelyX-Unicem (UN), RelyX-U100 (UC), GCem (GC), Maxcem (MC), Set (SET)] and 2 conventional resin cements [RelyX-ARC(RX), Panavia F(PF)] were used. An additional group included the use of a two-step self-etching adhesive (SE Bond) with Panavia F (PS). One hundred ninety-two molars were assigned to 8 groups according to luting material. Five-mm-thick composite disks were cemented and assigned to 3 subgroups according to water-exposure condition (n = 6): 24-h peripheral exposure (24h-PE-enamel margins), or 1 year of peripheral (1 yr-PE) or direct exposure (1 yr-DE-dentin margin). Restored teeth were sectioned into beams and tested in tension at 1 mm/min. Data were analyzed by two-way ANOVA and Tukey's test. Two additional specimens in each group were prepared for nanoleakage evaluation. Nanoleakage patterns were observed under SEM/TEM.
RESULTS: Except for RX, no significant reduction in µTBS was observed between 24h-PE and 1 yr-PE. 1 yr-DE reduced µTBS for RX, PF, GC, MC, and SET. No significant reduction in µTBS was observed for PS, UC, and UN after 1 year. After 1 yr-DE, RX and PS presented the highest µTBS, and SET and MC the lowest. Nanoleakage was reduced when there was a peripheral enamel margin. SET and MC presented more silver deposition than other groups.
CONCLUSION: The presence of a peripheral enamel margin reduced the degradation rate in resin/dentin interfaces for most materials. The µTBS values produced by the multi-step luting agents RX and PS were significantly higher than those observed for self-adhesive cement.