[Occluding effects of three new calcium desensitizers on dentinal tubules in vitro].
Аннотация на английскомСтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Xiong Zheng-hui, Xia Lu, Mei Lei, Han Guang-zheng, Chen Ya-ming
Аннотация
OBJECTIVE: To evaluate the occluding effects of three new calcium desensitizers on dentinal tubules in vitro.
METHODS: Twenty-five dentin specimens of 1.00 mm thick from freshly extracted third molars were divided into five groups randomly. After treatment with 6% citric acid, group A was treated with distilled water, and group B-E were treated with NovaMin, Pro-Argin, casein phosphopeptide-amorphous calcium phosphate (CPP-ACP), and 75% NaF glycerin for 2 min respectively. Then the teeth were vertically cleaved into two sections. The surfaces and cross sections were observed by the scanning electron microscope (SEM) and energy dispersive X-ray (EDX), which were analyzed by the Image-Pro Plus software.
RESULTS: The percentage of dentin tubules sealed were (81.6 ± 6.1)%, (71.5 ± 6.3)%, (43.2 ± 2.6)%, (39.9 ± 4.1)% for groups B, C, D and E respectively, and the occluding depth were (30.33 ± 2.26), (24.55 ± 2.58), (16.10 ± 4.65) and (8.90 ± 1.51) µm respectively. The differences between these groups were statistically significant (P < 0.01) except for group B and C (P > 0.05). However, there was no significant difference between all the groups for the Ca/P ratios (P = 0.342).
CONCLUSIONS: NovaMin may have better immediate occluding effects than other desensitizers and could deposit a dentin-like mineral.
METHODS: Twenty-five dentin specimens of 1.00 mm thick from freshly extracted third molars were divided into five groups randomly. After treatment with 6% citric acid, group A was treated with distilled water, and group B-E were treated with NovaMin, Pro-Argin, casein phosphopeptide-amorphous calcium phosphate (CPP-ACP), and 75% NaF glycerin for 2 min respectively. Then the teeth were vertically cleaved into two sections. The surfaces and cross sections were observed by the scanning electron microscope (SEM) and energy dispersive X-ray (EDX), which were analyzed by the Image-Pro Plus software.
RESULTS: The percentage of dentin tubules sealed were (81.6 ± 6.1)%, (71.5 ± 6.3)%, (43.2 ± 2.6)%, (39.9 ± 4.1)% for groups B, C, D and E respectively, and the occluding depth were (30.33 ± 2.26), (24.55 ± 2.58), (16.10 ± 4.65) and (8.90 ± 1.51) µm respectively. The differences between these groups were statistically significant (P < 0.01) except for group B and C (P > 0.05). However, there was no significant difference between all the groups for the Ca/P ratios (P = 0.342).
CONCLUSIONS: NovaMin may have better immediate occluding effects than other desensitizers and could deposit a dentin-like mineral.