Assessment of Microleakage Using Dye Penetration Method in Primary Teeth Restored with Tooth-colored Materials: An In Vitro Study.

AIM: The present study aimed to assess the microleakage in primary teeth restored with tooth-colored materials using the dye penetration method.

MATERIALS AND

METHODS

A total of 60 healthy primary molar teeth were included in this study and standardized class II mesio-occlusal cavities were prepared on the samples. Consequently, these teeth were randomly divided into three experimental groups (n = 20 each group) such as group I: nano-filled resin-modified glass-ionomer, group II: nanocomposite resin, and group III: Cention N. After completing all the restorations, the restored teeth were subjected to 100 cycles of thermocycling. Next, all the surfaces of the tooth, except the restoration and a 1-mm zone adjacent to the restoration's margins, were covered with two coats of nail varnish. The coated teeth were then submerged in a 0.5% basic fuchsin dye solution. The teeth were then sectioned along the center of each restoration mesiodistally. Each part was visualized under a stereomicroscope at ×40 magnifications to assess microleakage.

RESULTS

Out of all the included restorative materials, the least microleakage was demonstrated by teeth restored by the nano-filled resin-modified glass-ionomer (RMGI) group (1.05 ± 0.21) followed by the Cention N group (1.84 ± 0.14) and the nanocomposite resin group (3.10 ± 0.03). A statistical method involving the analysis of variance revealed a statistically significant difference among the different restorative materials. Multiple comparisons among the restorative materials showed a statistically significant difference between groups I and II and groups II and III restorative materials (p < 0.05). The dye penetration score 1 was more [11(55%)] for the nano-filled RMGI group, score 3 was more [12(60%)] for the nanocomposite resin group, and score 2 was more [9(45%)] for the Cention N group.

CONCLUSION

The present study showed significantly less microleakage associated with the nano-filled resin-modified glass ionomer group than nanocomposite resin and Cention N groups.

CLINICAL SIGNIFICANCE: Since many years, dentists have encountered a challenging problem with cervical lesions. Thus, an interdisciplinary treatment approach is the appropriate option in the management of carious teeth that involve gingival recession and cervical extension.