Corneal crosslinking with riboflavin using sunlight.

PURPOSE: To assess whether sunlight might be used to induce a biomechanical stiffening effect in riboflavin-soaked corneas similar to the effect observed in corneal crosslinking (CXL) using riboflavin and UV-A light.

SETTING

Center for Applied Biotechnology and Molecular Medicine, University of Zurich, Zurich, Switzerland.

DESIGN

Experimental study.

METHODS

52 porcine eyes were assayed. The concentration of riboflavin in the corneal stroma was estimated using UV-A transmission in a preliminary experiment. Then, the duration of sunlight exposure to achieve a fluence of 7.2/cm 2 was calculated. Finally, de-epithelialized corneas were divided equally into 3 groups and soaked with riboflavin 0.1% (control group and Group 1) or 0.5% (Group 2). Eyes from Groups 1 and 2 were then exposed to sunlight. The elastic modulus was calculated as an indicator of stiffness.

RESULTS

Riboflavin concentration in Group B was higher by a factor of 2.8 than Group A. According to live illuminance measurements and stromal riboflavin concentration, the sunlight exposure duration varied between 16 minutes and 45 minutes. Groups 1 and 2 had higher elastic modulus than controls ( P < .0001) but did not differ between them ( P = .194). The stiffening effect was 84% and 55%, respectively.

CONCLUSIONS

Sunlight exposure of ex vivo corneas soaked in both riboflavin 0.1% and 0.5% resulted in increased corneal stiffness. Specifically, riboflavin 0.1% with longer UV-A exposure showed a trend for a greater stiffening effect, which might open new alleys for the use of oral riboflavin and fractioned sunlight exposure as less invasive CXL techniques.